Crystallography Open Database
Search results
Result: there are 528453 entries in the selection
Switch to the old layout of the pageDownload all results as: list of COD numbers | list of CIF URLs | data in CSV format
We are unable to provide that many records as a single archive.
You can instead download the entire COD archive as a single .zip, .tgz or .txz archive.
Displaying all data in COD
COD ID  |
Links | Formula  |
Space group |
Cell parameters | Cell volume |
Bibliography |
|---|---|---|---|---|---|---|
| 9012912 | CIF | H | P 63/m m c | 3.313; 3.313; 5.383 90; 90; 120 | 51.168 | Vindryevsky, B. A.; Ishmaev, S. N.; Sadikov, I. P.; Chernyshev, A. A. Neutron diffraction studies of solid parahydrogen at pressures up to 5 kbar Sample: P = .28 GPa, T = 30 K Physics Letters, 1980, 355-358 |
| 9012913 | CIF | H | P 63/m m c | 3.308; 3.308; 5.377 90; 90; 120 | 50.957 | Vindryevsky, B. A.; Ishmaev, S. N.; Sadikov, I. P.; Chernyshev, A. A. Neutron diffraction studies of solid parahydrogen at pressures up to 5 kbar Sample: P = .3 GPa, T = 16.6 K Physics Letters, 1980, 355-358 |
| 9012914 | CIF | H | P 63/m m c | 3.216; 3.216; 5.219 90; 90; 120 | 46.747 | Vindryevsky, B. A.; Ishmaev, S. N.; Sadikov, I. P.; Chernyshev, A. A. Neutron diffraction studies of solid parahydrogen at pressures up to 5 kbar Sample: P = .48 GPa, T = 16.6 K Physics Letters, 1980, 355-358 |
| 9012915 | CIF | H | P 63/m m c | 3.223; 3.223; 5.234 90; 90; 120 | 47.085 | Vindryevsky, B. A.; Ishmaev, S. N.; Sadikov, I. P.; Chernyshev, A. A. Neutron diffraction studies of solid parahydrogen at pressures up to 5 kbar Sample: P = .5 GPa, T = 57.4 K Physics Letters, 1980, 355-358 |
| 9012916 | CIF | Ca | I m -3 m | 3.559; 3.559; 3.559 90; 90; 90 | 45.08 | Olijnyk, H.; Holzapfel, W. B. Phase transitions in alkaline earth metals under pressure Sample: P = 26.5 GPa Physics Letters, 1984, 191-194 |
| 9012917 | CIF | Ca | P m -3 m | 2.615; 2.615; 2.615 90; 90; 90 | 17.882 | Olijnyk, H.; Holzapfel, W. B. Phase transitions in alkaline earth metals under pressure Sample: P = 39 GPa Physics Letters, 1984, 191-194 |
| 9012918 | CIF | Si | P 6/m m m | 2.527; 2.527; 2.373 90; 90; 120 | 13.123 | Olijnyk, H.; Sikka, S. K.; Holzapfel, W. B. Structural phase transitions in Si and Ge under pressures up to 50 GPa Sample: at P = 19.5 GPa Note: phase V, structure stable between 16 GPa & 34 GPa Physics Letters, 1984, 137-140 |
| 9012919 | CIF | Si | P 63/m m c | 2.444; 2.444; 4.152 90; 90; 120 | 21.478 | Olijnyk, H.; Sikka, S. K.; Holzapfel, W. B. Structural phase transitions in Si and Ge under pressures up to 50 GPa Sample: at P = 43 GPa Note: phase VII, structure stable above 43 GPa Physics Letters, 1984, 137-140 |
| 9012920 | CIF | As3 Fe4 H18 O23 | P -4 3 m | 7.94; 7.94; 7.94 90; 90; 90 | 500.566 | Zemann, J. Uber die struktur des pharmakosiderits Note: the K atom could not be located Experientia, 1947, 3, 452-452 |
| 9012921 | CIF | Ca9 H22 O32 Si6 | P -1 | 10.576; 7.265; 10.931 101.3; 96.98; 109.65 | 759.496 | Bonaccorsi, E.; Merlino, S.; Taylor, H. F. W. The crystal structure of jennite, Ca9Si6O18(OH)6*8H2O Cement and Concrete Research, 2004, 34, 1481-1488 |
| 9012922 | CIF | Al2 Ca6 H60.602 O49.496 S3 | P 3 1 c | 11.166881; 11.166881; 21.35366 90; 90; 120 | 2306.04 | Hartman, M. R.; Berliner, R. Investigation of the structure of ettringite by time-of-flight neutron powder diffraction techniques Locality: synthetic Cement and Concrete Research, 2006, 36, 364-370 |
| 9012923 | CIF | C5 H18 N4 O21 P4 Sc3 | P 1 21/n 1 | 8.603; 15.476; 16.504 90; 96.877; 90 | 2181.53 | Bull, I.; Young, V.; Teat, S. J.; Peng, L.; Grey, C. P.; Parise, J. B. Hydrothermal synthesis and structural characterization of four scandium phosphate frameworks Chemistry of Materials, 2003, 15, 3818-3825 |
| 9012924 | CIF | Ti | I m -3 m | 3.282; 3.282; 3.282 90; 90; 90 | 35.352 | Levinger, B. W. Lattice parameters of beta titanium at room temperature Sample: at T = 298 K, known as the beta phase Journal of Metals, 1953, 5, 195-195 |
| 9012925 | CIF | Ti | P 6/m m m | 4.6; 4.6; 2.82 90; 90; 120 | 51.677 | Chebotareva, E. S.; Nuzhdina, S. G. Observation of omega-titanium in a composite hard facing alloy based on fine-grain diamonds Sample: at P = 4 GPa, known as the omega phase Fizika Metallov i Metallovedenie, 1973, 36, 200-202 |
| 9012926 | CIF | Co | F m -3 m | 3.5688; 3.5688; 3.5688 90; 90; 90 | 45.453 | Kohlhaas, R.; Dunner Ph; Schmitz-Pranghe N Uber die temperaturabhangigkeit der gitterparameter von eisen, kobalt und nickel im bereich hoher temperaturen Sample: at T = 520 C Zeitschrift fur Angewandte Physik, 1967, 23, 245-249 |
| 9012927 | CIF | Co | F m -3 m | 3.572; 3.572; 3.572 90; 90; 90 | 45.576 | Kohlhaas, R.; Dunner Ph; Schmitz-Pranghe N Uber die temperaturabhangigkeit der gitterparameter von eisen, kobalt und nickel im bereich hoher temperaturen Sample: at T = 598 C Zeitschrift fur Angewandte Physik, 1967, 23, 245-249 |
| 9012928 | CIF | Co | F m -3 m | 3.573; 3.573; 3.573 90; 90; 90 | 45.614 | Kohlhaas, R.; Dunner Ph; Schmitz-Pranghe N Uber die temperaturabhangigkeit der gitterparameter von eisen, kobalt und nickel im bereich hoher temperaturen Sample: at T = 647 C Zeitschrift fur Angewandte Physik, 1967, 23, 245-249 |
| 9012929 | CIF | Co | F m -3 m | 3.5755; 3.5755; 3.5755 90; 90; 90 | 45.71 | Kohlhaas, R.; Dunner Ph; Schmitz-Pranghe N Uber die temperaturabhangigkeit der gitterparameter von eisen, kobalt und nickel im bereich hoher temperaturen Sample: at T = 680 C Zeitschrift fur Angewandte Physik, 1967, 23, 245-249 |
| 9012930 | CIF | Co | F m -3 m | 3.577; 3.577; 3.577 90; 90; 90 | 45.767 | Kohlhaas, R.; Dunner Ph; Schmitz-Pranghe N Uber die temperaturabhangigkeit der gitterparameter von eisen, kobalt und nickel im bereich hoher temperaturen Sample: at T = 694 C Zeitschrift fur Angewandte Physik, 1967, 23, 245-249 |
| 9012931 | CIF | Co | F m -3 m | 3.5784; 3.5784; 3.5784 90; 90; 90 | 45.821 | Kohlhaas, R.; Dunner Ph; Schmitz-Pranghe N Uber die temperaturabhangigkeit der gitterparameter von eisen, kobalt und nickel im bereich hoher temperaturen Sample: at T = 719 C Zeitschrift fur Angewandte Physik, 1967, 23, 245-249 |
| 9012932 | CIF | Co | F m -3 m | 3.5834; 3.5834; 3.5834 90; 90; 90 | 46.014 | Kohlhaas, R.; Dunner Ph; Schmitz-Pranghe N Uber die temperaturabhangigkeit der gitterparameter von eisen, kobalt und nickel im bereich hoher temperaturen Sample: at T = 821 C Zeitschrift fur Angewandte Physik, 1967, 23, 245-249 |
| 9012933 | CIF | Co | F m -3 m | 3.5835; 3.5835; 3.5835 90; 90; 90 | 46.017 | Kohlhaas, R.; Dunner Ph; Schmitz-Pranghe N Uber die temperaturabhangigkeit der gitterparameter von eisen, kobalt und nickel im bereich hoher temperaturen Sample: at T = 861 C Zeitschrift fur Angewandte Physik, 1967, 23, 245-249 |
| 9012934 | CIF | Co | F m -3 m | 3.5863; 3.5863; 3.5863 90; 90; 90 | 46.125 | Kohlhaas, R.; Dunner Ph; Schmitz-Pranghe N Uber die temperaturabhangigkeit der gitterparameter von eisen, kobalt und nickel im bereich hoher temperaturen Sample: at T = 907 C Zeitschrift fur Angewandte Physik, 1967, 23, 245-249 |
| 9012935 | CIF | Co | F m -3 m | 3.59; 3.59; 3.59 90; 90; 90 | 46.268 | Kohlhaas, R.; Dunner Ph; Schmitz-Pranghe N Uber die temperaturabhangigkeit der gitterparameter von eisen, kobalt und nickel im bereich hoher temperaturen Sample: at T = 1003 C Zeitschrift fur Angewandte Physik, 1967, 23, 245-249 |
| 9012936 | CIF | Co | F m -3 m | 3.5914; 3.5914; 3.5914 90; 90; 90 | 46.322 | Kohlhaas, R.; Dunner Ph; Schmitz-Pranghe N Uber die temperaturabhangigkeit der gitterparameter von eisen, kobalt und nickel im bereich hoher temperaturen Sample: at T = 1027 C Zeitschrift fur Angewandte Physik, 1967, 23, 245-249 |
| 9012937 | CIF | Co | F m -3 m | 3.5921; 3.5921; 3.5921 90; 90; 90 | 46.35 | Kohlhaas, R.; Dunner Ph; Schmitz-Pranghe N Uber die temperaturabhangigkeit der gitterparameter von eisen, kobalt und nickel im bereich hoher temperaturen Sample: at T = 1049 C Zeitschrift fur Angewandte Physik, 1967, 23, 245-249 |
| 9012938 | CIF | Co | F m -3 m | 3.5956; 3.5956; 3.5956 90; 90; 90 | 46.485 | Kohlhaas, R.; Dunner Ph; Schmitz-Pranghe N Uber die temperaturabhangigkeit der gitterparameter von eisen, kobalt und nickel im bereich hoher temperaturen Sample: at T = 1082 C Zeitschrift fur Angewandte Physik, 1967, 23, 245-249 |
| 9012939 | CIF | Co | F m -3 m | 3.5957; 3.5957; 3.5957 90; 90; 90 | 46.489 | Kohlhaas, R.; Dunner Ph; Schmitz-Pranghe N Uber die temperaturabhangigkeit der gitterparameter von eisen, kobalt und nickel im bereich hoher temperaturen Sample: at T = 1098 C Zeitschrift fur Angewandte Physik, 1967, 23, 245-249 |
| 9012940 | CIF | Co | F m -3 m | 3.5979; 3.5979; 3.5979 90; 90; 90 | 46.574 | Kohlhaas, R.; Dunner Ph; Schmitz-Pranghe N Uber die temperaturabhangigkeit der gitterparameter von eisen, kobalt und nickel im bereich hoher temperaturen Sample: at T = 1117 C Zeitschrift fur Angewandte Physik, 1967, 23, 245-249 |
| 9012941 | CIF | Co | F m -3 m | 3.5987; 3.5987; 3.5987 90; 90; 90 | 46.605 | Kohlhaas, R.; Dunner Ph; Schmitz-Pranghe N Uber die temperaturabhangigkeit der gitterparameter von eisen, kobalt und nickel im bereich hoher temperaturen Sample: at T = 1128 C Zeitschrift fur Angewandte Physik, 1967, 23, 245-249 |
| 9012942 | CIF | Co | F m -3 m | 3.6007; 3.6007; 3.6007 90; 90; 90 | 46.683 | Kohlhaas, R.; Dunner Ph; Schmitz-Pranghe N Uber die temperaturabhangigkeit der gitterparameter von eisen, kobalt und nickel im bereich hoher temperaturen Sample: at T = 1142 C Zeitschrift fur Angewandte Physik, 1967, 23, 245-249 |
| 9012943 | CIF | Co | F m -3 m | 3.6023; 3.6023; 3.6023 90; 90; 90 | 46.745 | Kohlhaas, R.; Dunner Ph; Schmitz-Pranghe N Uber die temperaturabhangigkeit der gitterparameter von eisen, kobalt und nickel im bereich hoher temperaturen Sample: at T = 1160 C Zeitschrift fur Angewandte Physik, 1967, 23, 245-249 |
| 9012944 | CIF | Co | F m -3 m | 3.6052; 3.6052; 3.6052 90; 90; 90 | 46.858 | Kohlhaas, R.; Dunner Ph; Schmitz-Pranghe N Uber die temperaturabhangigkeit der gitterparameter von eisen, kobalt und nickel im bereich hoher temperaturen Sample: at T = 1191 C Zeitschrift fur Angewandte Physik, 1967, 23, 245-249 |
| 9012945 | CIF | Co | F m -3 m | 3.6064; 3.6064; 3.6064 90; 90; 90 | 46.905 | Kohlhaas, R.; Dunner Ph; Schmitz-Pranghe N Uber die temperaturabhangigkeit der gitterparameter von eisen, kobalt und nickel im bereich hoher temperaturen Sample: at T = 1201 C Zeitschrift fur Angewandte Physik, 1967, 23, 245-249 |
| 9012946 | CIF | Co | F m -3 m | 3.6102; 3.6102; 3.6102 90; 90; 90 | 47.054 | Kohlhaas, R.; Dunner Ph; Schmitz-Pranghe N Uber die temperaturabhangigkeit der gitterparameter von eisen, kobalt und nickel im bereich hoher temperaturen Sample: at T = 1253 C Zeitschrift fur Angewandte Physik, 1967, 23, 245-249 |
| 9012947 | CIF | Co | F m -3 m | 3.6148; 3.6148; 3.6148 90; 90; 90 | 47.234 | Kohlhaas, R.; Dunner Ph; Schmitz-Pranghe N Uber die temperaturabhangigkeit der gitterparameter von eisen, kobalt und nickel im bereich hoher temperaturen Sample: at T = 1312 C Zeitschrift fur Angewandte Physik, 1967, 23, 245-249 |
| 9012948 | CIF | Co | F m -3 m | 3.6214; 3.6214; 3.6214 90; 90; 90 | 47.493 | Kohlhaas, R.; Dunner Ph; Schmitz-Pranghe N Uber die temperaturabhangigkeit der gitterparameter von eisen, kobalt und nickel im bereich hoher temperaturen Sample: at T = 1398 C Zeitschrift fur Angewandte Physik, 1967, 23, 245-249 |
| 9012949 | CIF | Co | F m -3 m | 3.5441; 3.5441; 3.5441 90; 90; 90 | 44.516 | Owen, E. A.; Madoc Jones, D. Effect of grain size on the crystal structure of cobalt Sample: at T = 18 C Proceedings of the Physical Society of London, 1954, 67, 459-466 |
| 9012950 | CIF | Co | P 63/m m c | 2.5054; 2.5054; 4.0893 90; 90; 120 | 22.23 | Owen, E. A.; Madoc Jones, D. Effect of grain size on the crystal structure of cobalt Sample: at T = 18 C Note: quenched from above 450 C Proceedings of the Physical Society of London, 1954, 67, 459-466 |
| 9012951 | CIF | K O5 P Ti | P n a 21 | 12.49; 6.324; 10.069 90; 90; 90 | 795.318 | Allan, D. R.; Nelmes, R. J. The structural pressure dependence of potassium titanyl phosphate (KTP) to 8 GPa Sample: P = 6.3 GPa Journal of Physics: Condensed Matter, 1996, 8, 2337-2363 |
| 9012952 | CIF | K O5 P Ti | P n a 21 | 12.387; 6.311; 9.966 90; 90; 90 | 779.086 | Allan, D. R.; Nelmes, R. J. The structural pressure dependence of potassium titanyl phosphate (KTP) to 8 GPa Sample: P = 8.2 GPa Journal of Physics: Condensed Matter, 1996, 8, 2337-2363 |
| 9012953 | CIF | Au | F m -3 m | 4.0699; 4.0699; 4.0699 90; 90; 90 | 67.414 | Owen, E. A.; Yates, E. L. Precision measurements of crystal parameters Sample: at T = 18 C Note: lattice parameter is mean value of 5 radiation types Philosophical Magazine, 1933, 15, 472-488 |
| 9012954 | CIF | Cu | F m -3 m | 3.6077; 3.6077; 3.6077 90; 90; 90 | 46.956 | Owen, E. A.; Yates, E. L. Precision measurements of crystal parameters Sample: at T = 18 C Note: lattice parameter is mean value of 2 radiation types Philosophical Magazine, 1933, 15, 472-488 |
| 9012955 | CIF | Al | F m -3 m | 4.0406; 4.0406; 4.0406 90; 90; 90 | 65.969 | Owen, E. A.; Yates, E. L. Precision measurements of crystal parameters Locality: synthetic Sample: at T = 18 C Note: lattice parameter is mean value of 4 radiation types Philosophical Magazine, 1933, 15, 472-488 |
| 9012957 | CIF | Pt | F m -3 m | 3.9158; 3.9158; 3.9158 90; 90; 90 | 60.043 | Owen, E. A.; Yates, E. L. Precision measurements of crystal parameters Sample: at T = 18 C Note: lattice parameter is mean value of 5 radiation types Philosophical Magazine, 1933, 15, 472-488 |
| 9012958 | CIF | Rh | F m -3 m | 3.7957; 3.7957; 3.7957 90; 90; 90 | 54.686 | Owen, E. A.; Yates, E. L. Precision measurements of crystal parameters Sample: at T = 18 C Note: lattice parameter is mean value of 3 radiation types Philosophical Magazine, 1933, 15, 472-488 |
| 9012959 | CIF | Pb | F m -3 m | 4.9396; 4.9396; 4.9396 90; 90; 90 | 120.525 | Owen, E. A.; Yates, E. L. Precision measurements of crystal parameters Sample: at T = 18 C Note: lattice parameter is mean value of 4 radiation types Philosophical Magazine, 1933, 15, 472-488 |
| 9012960 | CIF | Ir | F m -3 m | 3.8312; 3.8312; 3.8312 90; 90; 90 | 56.235 | Owen, E. A.; Yates, E. L. Precision measurements of crystal parameters Sample: at T = 18 C Note: lattice parameter is mean value of 3 radiation types Philosophical Magazine, 1933, 15, 472-488 |
| 9012961 | CIF | Ag | F m -3 m | 4.0772; 4.0772; 4.0772 90; 90; 90 | 67.778 | Owen, E. A.; Yates, E. L. Precision measurements of crystal parameters Sample: at T = 18 C Note: lattice parameter is mean value of 5 radiation types Philosophical Magazine, 1933, 15, 472-488 |
| 9012962 | CIF | Pd | F m -3 m | 3.8824; 3.8824; 3.8824 90; 90; 90 | 58.52 | Owen, E. A.; Yates, E. L. Precision measurements of crystal parameters Sample: at T = 18 C Note: lattice parameter is mean value of 4 radiation types Philosophical Magazine, 1933, 15, 472-488 |
| 9012963 | CIF | Ni | F m -3 m | 3.517; 3.517; 3.517 90; 90; 90 | 43.503 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 12 C Note: film 601 & 617 Philosophical Magazine, 1936, 21, 809-819 |
| 9012964 | CIF | Ni | F m -3 m | 3.517; 3.517; 3.517 90; 90; 90 | 43.503 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 13 C Note: film 563 & 608 Philosophical Magazine, 1936, 21, 809-819 |
| 9012965 | CIF | Ni | F m -3 m | 3.517; 3.517; 3.517 90; 90; 90 | 43.503 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 14 C Note: films 569, 574, 596, 597 Philosophical Magazine, 1936, 21, 809-819 |
| 9012966 | CIF | Ni | F m -3 m | 3.517; 3.517; 3.517 90; 90; 90 | 43.503 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 15 C Note: films 560, 562, 621, 625, 626 Philosophical Magazine, 1936, 21, 809-819 |
| 9012967 | CIF | Ni | F m -3 m | 3.5171; 3.5171; 3.5171 90; 90; 90 | 43.507 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 16 C Note: film 590 Philosophical Magazine, 1936, 21, 809-819 |
| 9012968 | CIF | Ni | F m -3 m | 3.5172; 3.5172; 3.5172 90; 90; 90 | 43.51 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 18 C Philosophical Magazine, 1936, 21, 809-819 |
| 9012969 | CIF | Ni | F m -3 m | 3.5212; 3.5212; 3.5212 90; 90; 90 | 43.659 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 98 C Note: film 565 Philosophical Magazine, 1936, 21, 809-819 |
| 9012970 | CIF | Ni | F m -3 m | 3.5259; 3.5259; 3.5259 90; 90; 90 | 43.834 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 187 C Note: film 567 Philosophical Magazine, 1936, 21, 809-819 |
| 9012971 | CIF | Ni | F m -3 m | 3.5295; 3.5295; 3.5295 90; 90; 90 | 43.968 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 257 C Note: film 573 Philosophical Magazine, 1936, 21, 809-819 |
| 9012972 | CIF | Ni | F m -3 m | 3.5302; 3.5302; 3.5302 90; 90; 90 | 43.994 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 275 C Note: film 595 Philosophical Magazine, 1936, 21, 809-819 |
| 9012973 | CIF | Ni | F m -3 m | 3.5319; 3.5319; 3.5319 90; 90; 90 | 44.058 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 301 C Note: film 564 Philosophical Magazine, 1936, 21, 809-819 |
| 9012974 | CIF | Ni | F m -3 m | 3.5335; 3.5335; 3.5335 90; 90; 90 | 44.118 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 331 C Note: film 594 Philosophical Magazine, 1936, 21, 809-819 |
| 9012975 | CIF | Ni | F m -3 m | 3.5337; 3.5337; 3.5337 90; 90; 90 | 44.125 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 333 C Note: film 571 Philosophical Magazine, 1936, 21, 809-819 |
| 9012976 | CIF | Ni | F m -3 m | 3.5337; 3.5337; 3.5337 90; 90; 90 | 44.125 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 336 C Note: film 584 Philosophical Magazine, 1936, 21, 809-819 |
| 9012977 | CIF | Ni | F m -3 m | 3.5338; 3.5338; 3.5338 90; 90; 90 | 44.129 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 338 C Note: film 606 Philosophical Magazine, 1936, 21, 809-819 |
| 9012978 | CIF | Ni | F m -3 m | 3.5343; 3.5343; 3.5343 90; 90; 90 | 44.148 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 341 C Note: film 611 Philosophical Magazine, 1936, 21, 809-819 |
| 9012979 | CIF | Ni | F m -3 m | 3.5343; 3.5343; 3.5343 90; 90; 90 | 44.148 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 342 C Note: film 585 Philosophical Magazine, 1936, 21, 809-819 |
| 9012980 | CIF | Ni | F m -3 m | 3.5342; 3.5342; 3.5342 90; 90; 90 | 44.144 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 343 C Note: film 618 Philosophical Magazine, 1936, 21, 809-819 |
| 9012981 | CIF | Ni | F m -3 m | 3.5345; 3.5345; 3.5345 90; 90; 90 | 44.155 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 345 C Note: film 616 & 610 Philosophical Magazine, 1936, 21, 809-819 |
| 9012982 | CIF | Ni | F m -3 m | 3.5347; 3.5347; 3.5347 90; 90; 90 | 44.163 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 346 C Note: film 614 Philosophical Magazine, 1936, 21, 809-819 |
| 9012983 | CIF | Ni | F m -3 m | 3.5346; 3.5346; 3.5346 90; 90; 90 | 44.159 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 348 C Note: film 605 Philosophical Magazine, 1936, 21, 809-819 |
| 9012984 | CIF | Ni | F m -3 m | 3.5347; 3.5347; 3.5347 90; 90; 90 | 44.163 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 349 C Note: film 586 Philosophical Magazine, 1936, 21, 809-819 |
| 9012985 | CIF | Ni | F m -3 m | 3.535; 3.535; 3.535 90; 90; 90 | 44.174 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 352 C Note: film 612 Philosophical Magazine, 1936, 21, 809-819 |
| 9012986 | CIF | Ni | F m -3 m | 3.5355; 3.5355; 3.5355 90; 90; 90 | 44.193 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 356 C Note: film 624 Philosophical Magazine, 1936, 21, 809-819 |
| 9012987 | CIF | Ni | F m -3 m | 3.5356; 3.5356; 3.5356 90; 90; 90 | 44.197 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 359 C Note: film 592 Philosophical Magazine, 1936, 21, 809-819 |
| 9012988 | CIF | Ni | F m -3 m | 3.5359; 3.5359; 3.5359 90; 90; 90 | 44.208 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 362 C Note: film 599 Philosophical Magazine, 1936, 21, 809-819 |
| 9012989 | CIF | Ni | F m -3 m | 3.536; 3.536; 3.536 90; 90; 90 | 44.212 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 363 C Note: film 600 Philosophical Magazine, 1936, 21, 809-819 |
| 9012990 | CIF | Ni | F m -3 m | 3.5361; 3.5361; 3.5361 90; 90; 90 | 44.215 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 365 C Note: film 593 Philosophical Magazine, 1936, 21, 809-819 |
| 9012991 | CIF | Ni | F m -3 m | 3.5367; 3.5367; 3.5367 90; 90; 90 | 44.238 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 370 C Note: film 577 & 598 Philosophical Magazine, 1936, 21, 809-819 |
| 9012992 | CIF | Ni | F m -3 m | 3.5367; 3.5367; 3.5367 90; 90; 90 | 44.238 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 373 C Note: film 576 Philosophical Magazine, 1936, 21, 809-819 |
| 9012993 | CIF | Ni | F m -3 m | 3.5367; 3.5367; 3.5367 90; 90; 90 | 44.238 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 374 C Note: film 603 Philosophical Magazine, 1936, 21, 809-819 |
| 9012994 | CIF | Ni | F m -3 m | 3.5371; 3.5371; 3.5371 90; 90; 90 | 44.253 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 378 C Note: film 604 Philosophical Magazine, 1936, 21, 809-819 |
| 9012995 | CIF | Ni | F m -3 m | 3.5379; 3.5379; 3.5379 90; 90; 90 | 44.283 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 388 C Note: film 589 Philosophical Magazine, 1936, 21, 809-819 |
| 9012996 | CIF | Ni | F m -3 m | 3.5383; 3.5383; 3.5383 90; 90; 90 | 44.298 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 398 C Note: film 556 Philosophical Magazine, 1936, 21, 809-819 |
| 9012997 | CIF | Ni | F m -3 m | 3.5386; 3.5386; 3.5386 90; 90; 90 | 44.309 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 405 C Note: film 613 Philosophical Magazine, 1936, 21, 809-819 |
| 9012998 | CIF | Ni | F m -3 m | 3.5388; 3.5388; 3.5388 90; 90; 90 | 44.317 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 410 C Note: film 607 Philosophical Magazine, 1936, 21, 809-819 |
| 9012999 | CIF | Ni | F m -3 m | 3.5388; 3.5388; 3.5388 90; 90; 90 | 44.317 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample at T = 411 C Note: film 609 Philosophical Magazine, 1936, 21, 809-819 |
| 9013000 | CIF | Ni | F m -3 m | 3.5402; 3.5402; 3.5402 90; 90; 90 | 44.369 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 429 C Note: film 591 Philosophical Magazine, 1936, 21, 809-819 |
| 9013001 | CIF | Ni | F m -3 m | 3.5422; 3.5422; 3.5422 90; 90; 90 | 44.445 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 460 C Note: film 572 Philosophical Magazine, 1936, 21, 809-819 |
| 9013002 | CIF | Ni | F m -3 m | 3.5448; 3.5448; 3.5448 90; 90; 90 | 44.543 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 501 C Note: film 561 Philosophical Magazine, 1936, 21, 809-819 |
| 9013003 | CIF | Ni | F m -3 m | 3.5481; 3.5481; 3.5481 90; 90; 90 | 44.667 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 557 C Note: film 575 Philosophical Magazine, 1936, 21, 809-819 |
| 9013004 | CIF | Ni | F m -3 m | 3.5508; 3.5508; 3.5508 90; 90; 90 | 44.769 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 603 C Note: film 568 Philosophical Magazine, 1936, 21, 809-819 |
| 9013005 | CIF | Ni | F m -3 m | 3.5516; 3.5516; 3.5516 90; 90; 90 | 44.799 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 608 C Note: film 615 Philosophical Magazine, 1936, 21, 809-819 |
| 9013006 | CIF | As | B m a b | 3.65; 4.47; 11 90; 90; 90 | 179.471 | Smith, P. M.; Leadbetter, A. J.; Apling, A. J. The structures of orthorhombic and vitrous arsenic Locality: synthetic Note: known as arsenolamprite Philosophical Magazine, 1975, 31, 57-64 |
| 9013007 | CIF | Ni | P 63/m m c | 2.622; 2.622; 4.321 90; 90; 120 | 25.726 | Weik, H.; Hemenger, P. Existence of the hexagonal modification of nickel Locality: synthetic Bulletin of the American Physical Society, 1965, 10, 1140-1140 |
| 9013008 | CIF | Sb | P m -3 m | 3.16; 3.16; 3.16 90; 90; 90 | 31.554 | Akhtar, D.; Vankar, V. D.; Goel, T. C.; Chopra, K. L. Metastable structures of liquid-quenched and vapour-quenched antimony films Note: liquid-quenched specimen Journal of Materials Science, 1979, 14, 988-994 |
| 9013009 | CIF | Sb | F m -3 m | 4.61; 4.61; 4.61 90; 90; 90 | 97.972 | Akhtar, D.; Vankar, V. D.; Goel, T. C.; Chopra, K. L. Metastable structures of liquid-quenched and vapour-quenched antimony films Locality: synthetic Note: liquid-quenched specimen Journal of Materials Science, 1979, 14, 988-994 |
| 9013010 | CIF | Sb | I 4/m m m | 3.01; 3.01; 4.96 90; 90; 90 | 44.938 | Akhtar, D.; Vankar, V. D.; Goel, T. C.; Chopra, K. L. Metastable structures of liquid-quenched and vapour-quenched antimony films Note: liquid-quenched specimen Journal of Materials Science, 1979, 14, 988-994 |
| 9013011 | CIF | Sb | P 63/m m c | 3.33; 3.33; 5.23 90; 90; 120 | 50.225 | Akhtar, D.; Vankar, V. D.; Goel, T. C.; Chopra, K. L. Metastable structures of liquid-quenched and vapour-quenched antimony films Locality: synthetic Note: liquid-quenched specimen Note: HCP structure resulted from electron beam heating of the tetragonal, FCC and SC structures Journal of Materials Science, 1979, 14, 988-994 |
| 9013014 | CIF | Cu | F m -3 m | 3.613; 3.613; 3.613 90; 90; 90 | 47.163 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 293 K Journal of Materials Science, 1988, 23, 757-760 |
Back to the search form
Your own data is not in the COD? Deposit it, thanks!