Crystallography Open Database
Search results
Result: there are 525804 entries in the selection
Switch to the old layout of the pageDownload all results as: list of COD numbers | list of CIF URLs | data in CSV format
We are unable to provide that many records as a single archive.
You can instead download the entire COD archive as a single .zip, .tgz or .txz archive.
Displaying all data in COD
COD ID  |
Links | Formula  |
Space group |
Cell parameters | Cell volume |
Bibliography |
|---|---|---|---|---|---|---|
| 9012962 | CIF | Pd | F m -3 m | 3.8824; 3.8824; 3.8824 90; 90; 90 | 58.52 | Owen, E. A.; Yates, E. L. Precision measurements of crystal parameters Sample: at T = 18 C Note: lattice parameter is mean value of 4 radiation types Philosophical Magazine, 1933, 15, 472-488 |
| 9012963 | CIF | Ni | F m -3 m | 3.517; 3.517; 3.517 90; 90; 90 | 43.503 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 12 C Note: film 601 & 617 Philosophical Magazine, 1936, 21, 809-819 |
| 9012964 | CIF | Ni | F m -3 m | 3.517; 3.517; 3.517 90; 90; 90 | 43.503 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 13 C Note: film 563 & 608 Philosophical Magazine, 1936, 21, 809-819 |
| 9012965 | CIF | Ni | F m -3 m | 3.517; 3.517; 3.517 90; 90; 90 | 43.503 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 14 C Note: films 569, 574, 596, 597 Philosophical Magazine, 1936, 21, 809-819 |
| 9012966 | CIF | Ni | F m -3 m | 3.517; 3.517; 3.517 90; 90; 90 | 43.503 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 15 C Note: films 560, 562, 621, 625, 626 Philosophical Magazine, 1936, 21, 809-819 |
| 9012967 | CIF | Ni | F m -3 m | 3.5171; 3.5171; 3.5171 90; 90; 90 | 43.507 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 16 C Note: film 590 Philosophical Magazine, 1936, 21, 809-819 |
| 9012968 | CIF | Ni | F m -3 m | 3.5172; 3.5172; 3.5172 90; 90; 90 | 43.51 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 18 C Philosophical Magazine, 1936, 21, 809-819 |
| 9012969 | CIF | Ni | F m -3 m | 3.5212; 3.5212; 3.5212 90; 90; 90 | 43.659 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 98 C Note: film 565 Philosophical Magazine, 1936, 21, 809-819 |
| 9012970 | CIF | Ni | F m -3 m | 3.5259; 3.5259; 3.5259 90; 90; 90 | 43.834 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 187 C Note: film 567 Philosophical Magazine, 1936, 21, 809-819 |
| 9012971 | CIF | Ni | F m -3 m | 3.5295; 3.5295; 3.5295 90; 90; 90 | 43.968 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 257 C Note: film 573 Philosophical Magazine, 1936, 21, 809-819 |
| 9012972 | CIF | Ni | F m -3 m | 3.5302; 3.5302; 3.5302 90; 90; 90 | 43.994 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 275 C Note: film 595 Philosophical Magazine, 1936, 21, 809-819 |
| 9012973 | CIF | Ni | F m -3 m | 3.5319; 3.5319; 3.5319 90; 90; 90 | 44.058 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 301 C Note: film 564 Philosophical Magazine, 1936, 21, 809-819 |
| 9012974 | CIF | Ni | F m -3 m | 3.5335; 3.5335; 3.5335 90; 90; 90 | 44.118 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 331 C Note: film 594 Philosophical Magazine, 1936, 21, 809-819 |
| 9012975 | CIF | Ni | F m -3 m | 3.5337; 3.5337; 3.5337 90; 90; 90 | 44.125 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 333 C Note: film 571 Philosophical Magazine, 1936, 21, 809-819 |
| 9012976 | CIF | Ni | F m -3 m | 3.5337; 3.5337; 3.5337 90; 90; 90 | 44.125 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 336 C Note: film 584 Philosophical Magazine, 1936, 21, 809-819 |
| 9012977 | CIF | Ni | F m -3 m | 3.5338; 3.5338; 3.5338 90; 90; 90 | 44.129 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 338 C Note: film 606 Philosophical Magazine, 1936, 21, 809-819 |
| 9012978 | CIF | Ni | F m -3 m | 3.5343; 3.5343; 3.5343 90; 90; 90 | 44.148 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 341 C Note: film 611 Philosophical Magazine, 1936, 21, 809-819 |
| 9012979 | CIF | Ni | F m -3 m | 3.5343; 3.5343; 3.5343 90; 90; 90 | 44.148 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 342 C Note: film 585 Philosophical Magazine, 1936, 21, 809-819 |
| 9012980 | CIF | Ni | F m -3 m | 3.5342; 3.5342; 3.5342 90; 90; 90 | 44.144 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 343 C Note: film 618 Philosophical Magazine, 1936, 21, 809-819 |
| 9012981 | CIF | Ni | F m -3 m | 3.5345; 3.5345; 3.5345 90; 90; 90 | 44.155 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 345 C Note: film 616 & 610 Philosophical Magazine, 1936, 21, 809-819 |
| 9012982 | CIF | Ni | F m -3 m | 3.5347; 3.5347; 3.5347 90; 90; 90 | 44.163 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 346 C Note: film 614 Philosophical Magazine, 1936, 21, 809-819 |
| 9012983 | CIF | Ni | F m -3 m | 3.5346; 3.5346; 3.5346 90; 90; 90 | 44.159 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 348 C Note: film 605 Philosophical Magazine, 1936, 21, 809-819 |
| 9012984 | CIF | Ni | F m -3 m | 3.5347; 3.5347; 3.5347 90; 90; 90 | 44.163 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 349 C Note: film 586 Philosophical Magazine, 1936, 21, 809-819 |
| 9012985 | CIF | Ni | F m -3 m | 3.535; 3.535; 3.535 90; 90; 90 | 44.174 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 352 C Note: film 612 Philosophical Magazine, 1936, 21, 809-819 |
| 9012986 | CIF | Ni | F m -3 m | 3.5355; 3.5355; 3.5355 90; 90; 90 | 44.193 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 356 C Note: film 624 Philosophical Magazine, 1936, 21, 809-819 |
| 9012987 | CIF | Ni | F m -3 m | 3.5356; 3.5356; 3.5356 90; 90; 90 | 44.197 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 359 C Note: film 592 Philosophical Magazine, 1936, 21, 809-819 |
| 9012988 | CIF | Ni | F m -3 m | 3.5359; 3.5359; 3.5359 90; 90; 90 | 44.208 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 362 C Note: film 599 Philosophical Magazine, 1936, 21, 809-819 |
| 9012989 | CIF | Ni | F m -3 m | 3.536; 3.536; 3.536 90; 90; 90 | 44.212 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 363 C Note: film 600 Philosophical Magazine, 1936, 21, 809-819 |
| 9012990 | CIF | Ni | F m -3 m | 3.5361; 3.5361; 3.5361 90; 90; 90 | 44.215 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 365 C Note: film 593 Philosophical Magazine, 1936, 21, 809-819 |
| 9012991 | CIF | Ni | F m -3 m | 3.5367; 3.5367; 3.5367 90; 90; 90 | 44.238 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 370 C Note: film 577 & 598 Philosophical Magazine, 1936, 21, 809-819 |
| 9012992 | CIF | Ni | F m -3 m | 3.5367; 3.5367; 3.5367 90; 90; 90 | 44.238 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 373 C Note: film 576 Philosophical Magazine, 1936, 21, 809-819 |
| 9012993 | CIF | Ni | F m -3 m | 3.5367; 3.5367; 3.5367 90; 90; 90 | 44.238 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 374 C Note: film 603 Philosophical Magazine, 1936, 21, 809-819 |
| 9012994 | CIF | Ni | F m -3 m | 3.5371; 3.5371; 3.5371 90; 90; 90 | 44.253 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 378 C Note: film 604 Philosophical Magazine, 1936, 21, 809-819 |
| 9012995 | CIF | Ni | F m -3 m | 3.5379; 3.5379; 3.5379 90; 90; 90 | 44.283 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 388 C Note: film 589 Philosophical Magazine, 1936, 21, 809-819 |
| 9012996 | CIF | Ni | F m -3 m | 3.5383; 3.5383; 3.5383 90; 90; 90 | 44.298 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 398 C Note: film 556 Philosophical Magazine, 1936, 21, 809-819 |
| 9012997 | CIF | Ni | F m -3 m | 3.5386; 3.5386; 3.5386 90; 90; 90 | 44.309 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 405 C Note: film 613 Philosophical Magazine, 1936, 21, 809-819 |
| 9012998 | CIF | Ni | F m -3 m | 3.5388; 3.5388; 3.5388 90; 90; 90 | 44.317 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 410 C Note: film 607 Philosophical Magazine, 1936, 21, 809-819 |
| 9012999 | CIF | Ni | F m -3 m | 3.5388; 3.5388; 3.5388 90; 90; 90 | 44.317 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample at T = 411 C Note: film 609 Philosophical Magazine, 1936, 21, 809-819 |
| 9013000 | CIF | Ni | F m -3 m | 3.5402; 3.5402; 3.5402 90; 90; 90 | 44.369 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 429 C Note: film 591 Philosophical Magazine, 1936, 21, 809-819 |
| 9013001 | CIF | Ni | F m -3 m | 3.5422; 3.5422; 3.5422 90; 90; 90 | 44.445 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 460 C Note: film 572 Philosophical Magazine, 1936, 21, 809-819 |
| 9013002 | CIF | Ni | F m -3 m | 3.5448; 3.5448; 3.5448 90; 90; 90 | 44.543 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 501 C Note: film 561 Philosophical Magazine, 1936, 21, 809-819 |
| 9013003 | CIF | Ni | F m -3 m | 3.5481; 3.5481; 3.5481 90; 90; 90 | 44.667 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 557 C Note: film 575 Philosophical Magazine, 1936, 21, 809-819 |
| 9013004 | CIF | Ni | F m -3 m | 3.5508; 3.5508; 3.5508 90; 90; 90 | 44.769 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 603 C Note: film 568 Philosophical Magazine, 1936, 21, 809-819 |
| 9013005 | CIF | Ni | F m -3 m | 3.5516; 3.5516; 3.5516 90; 90; 90 | 44.799 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 608 C Note: film 615 Philosophical Magazine, 1936, 21, 809-819 |
| 9013006 | CIF | As | B m a b | 3.65; 4.47; 11 90; 90; 90 | 179.471 | Smith, P. M.; Leadbetter, A. J.; Apling, A. J. The structures of orthorhombic and vitrous arsenic Locality: synthetic Note: known as arsenolamprite Philosophical Magazine, 1975, 31, 57-64 |
| 9013007 | CIF | Ni | P 63/m m c | 2.622; 2.622; 4.321 90; 90; 120 | 25.726 | Weik, H.; Hemenger, P. Existence of the hexagonal modification of nickel Locality: synthetic Bulletin of the American Physical Society, 1965, 10, 1140-1140 |
| 9013008 | CIF | Sb | P m -3 m | 3.16; 3.16; 3.16 90; 90; 90 | 31.554 | Akhtar, D.; Vankar, V. D.; Goel, T. C.; Chopra, K. L. Metastable structures of liquid-quenched and vapour-quenched antimony films Note: liquid-quenched specimen Journal of Materials Science, 1979, 14, 988-994 |
| 9013009 | CIF | Sb | F m -3 m | 4.61; 4.61; 4.61 90; 90; 90 | 97.972 | Akhtar, D.; Vankar, V. D.; Goel, T. C.; Chopra, K. L. Metastable structures of liquid-quenched and vapour-quenched antimony films Locality: synthetic Note: liquid-quenched specimen Journal of Materials Science, 1979, 14, 988-994 |
| 9013010 | CIF | Sb | I 4/m m m | 3.01; 3.01; 4.96 90; 90; 90 | 44.938 | Akhtar, D.; Vankar, V. D.; Goel, T. C.; Chopra, K. L. Metastable structures of liquid-quenched and vapour-quenched antimony films Note: liquid-quenched specimen Journal of Materials Science, 1979, 14, 988-994 |
| 9013011 | CIF | Sb | P 63/m m c | 3.33; 3.33; 5.23 90; 90; 120 | 50.225 | Akhtar, D.; Vankar, V. D.; Goel, T. C.; Chopra, K. L. Metastable structures of liquid-quenched and vapour-quenched antimony films Locality: synthetic Note: liquid-quenched specimen Note: HCP structure resulted from electron beam heating of the tetragonal, FCC and SC structures Journal of Materials Science, 1979, 14, 988-994 |
| 9013014 | CIF | Cu | F m -3 m | 3.613; 3.613; 3.613 90; 90; 90 | 47.163 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 293 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013015 | CIF | Cu | F m -3 m | 3.63; 3.63; 3.63 90; 90; 90 | 47.832 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 577 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013016 | CIF | Cu | F m -3 m | 3.636; 3.636; 3.636 90; 90; 90 | 48.07 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 680 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013017 | CIF | Cu | F m -3 m | 3.644; 3.644; 3.644 90; 90; 90 | 48.388 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 777 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013018 | CIF | Cu | F m -3 m | 3.65; 3.65; 3.65 90; 90; 90 | 48.627 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 874 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013019 | CIF | Cu | F m -3 m | 3.658; 3.658; 3.658 90; 90; 90 | 48.948 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 979 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013020 | CIF | Cu | F m -3 m | 3.667; 3.667; 3.667 90; 90; 90 | 49.31 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 1076 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013021 | CIF | Cu | F m -3 m | 3.672; 3.672; 3.672 90; 90; 90 | 49.512 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 1179 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013022 | CIF | Cu | F m -3 m | 3.684; 3.684; 3.684 90; 90; 90 | 49.999 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 1275 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013023 | CIF | Cu | F m -3 m | 3.692; 3.692; 3.692 90; 90; 90 | 50.325 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 1343 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013024 | CIF | Ni | F m -3 m | 3.524; 3.524; 3.524 90; 90; 90 | 43.763 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 293 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013025 | CIF | Ni | F m -3 m | 3.538; 3.538; 3.538 90; 90; 90 | 44.287 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 578 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013026 | CIF | Ni | F m -3 m | 3.544; 3.544; 3.544 90; 90; 90 | 44.512 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 676 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013027 | CIF | Ni | F m -3 m | 3.552; 3.552; 3.552 90; 90; 90 | 44.815 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 825 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013028 | CIF | Ni | F m -3 m | 3.563; 3.563; 3.563 90; 90; 90 | 45.232 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 1007 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013029 | CIF | Ni | F m -3 m | 3.571; 3.571; 3.571 90; 90; 90 | 45.538 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 1123 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013030 | CIF | Ni | F m -3 m | 3.581; 3.581; 3.581 90; 90; 90 | 45.921 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 1256 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013031 | CIF | Ni | F m -3 m | 3.587; 3.587; 3.587 90; 90; 90 | 46.152 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 1345 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013032 | CIF | Ni | F m -3 m | 3.595; 3.595; 3.595 90; 90; 90 | 46.462 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 1433 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013033 | CIF | Ni | F m -3 m | 3.603; 3.603; 3.603 90; 90; 90 | 46.773 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 1553 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013034 | CIF | Ni | F m -3 m | 3.615; 3.615; 3.615 90; 90; 90 | 47.242 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 1676 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013035 | CIF | Au | F m -3 m | 4.072; 4.072; 4.072 90; 90; 90 | 67.519 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 293 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013036 | CIF | Au | F m -3 m | 4.091; 4.091; 4.091 90; 90; 90 | 68.468 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 574 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013037 | CIF | Au | F m -3 m | 4.097; 4.097; 4.097 90; 90; 90 | 68.77 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 676 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013038 | CIF | Au | F m -3 m | 4.103; 4.103; 4.103 90; 90; 90 | 69.072 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 777 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013039 | CIF | Au | F m -3 m | 4.11; 4.11; 4.11 90; 90; 90 | 69.427 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 875 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013040 | CIF | Au | F m -3 m | 4.117; 4.117; 4.117 90; 90; 90 | 69.782 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 971 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013041 | CIF | Au | F m -3 m | 4.125; 4.125; 4.125 90; 90; 90 | 70.189 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 1075 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013042 | CIF | Au | F m -3 m | 4.134; 4.134; 4.134 90; 90; 90 | 70.65 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 1179 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013043 | CIF | Au | F m -3 m | 4.141; 4.141; 4.141 90; 90; 90 | 71.009 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 1280 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013044 | CIF | Au | F m -3 m | 4.145; 4.145; 4.145 90; 90; 90 | 71.215 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 1324 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013045 | CIF | Ag | F m -3 m | 4.086; 4.086; 4.086 90; 90; 90 | 68.217 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 293 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013046 | CIF | Ag | F m -3 m | 4.109; 4.109; 4.109 90; 90; 90 | 69.376 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 576 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013047 | CIF | Ag | F m -3 m | 4.117; 4.117; 4.117 90; 90; 90 | 69.782 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 671 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013048 | CIF | Ag | F m -3 m | 4.126; 4.126; 4.126 90; 90; 90 | 70.241 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 774 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013049 | CIF | Ag | F m -3 m | 4.135; 4.135; 4.135 90; 90; 90 | 70.701 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 875 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013050 | CIF | Ag | F m -3 m | 4.144; 4.144; 4.144 90; 90; 90 | 71.164 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 975 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013051 | CIF | Ag | F m -3 m | 4.155; 4.155; 4.155 90; 90; 90 | 71.732 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 1076 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013052 | CIF | Ag | F m -3 m | 4.166; 4.166; 4.166 90; 90; 90 | 72.303 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 1174 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013053 | CIF | Ag | F m -3 m | 4.172; 4.172; 4.172 90; 90; 90 | 72.616 | Suh, I.-K.; Ohta, H.; Waseda, Y. High-temperature thermal expansion of six metallic elements measured by dilatation method and X-ray diffraction Sample: at T = 1228 K Journal of Materials Science, 1988, 23, 757-760 |
| 9013054 | CIF | Mg | P 63/m m c | 3.2017; 3.2017; 5.1986 90; 90; 120 | 46.151 | Raynor, G. V.; Hume-Rothery W A technique for the X-ray powder photography of reactive metals and alloys with special reference to the lattice spacing of magnesium at high temperatures Locality: synthetic Sample: at T = 10 C Note: experiment #4 Journal of the Institute of Metals, 1939, 65, 477-485 |
| 9013055 | CIF | Mg | P 63/m m c | 3.2032; 3.2032; 5.201 90; 90; 120 | 46.215 | Raynor, G. V.; Hume-Rothery W A technique for the X-ray powder photography of reactive metals and alloys with special reference to the lattice spacing of magnesium at high temperatures Locality: synthetic Sample: at T = 27.7 C Note: experiment #6 Journal of the Institute of Metals, 1939, 65, 477-485 |
| 9013056 | CIF | Mg | P 63/m m c | 3.2035; 3.2035; 5.2015 90; 90; 120 | 46.228 | Raynor, G. V.; Hume-Rothery W A technique for the X-ray powder photography of reactive metals and alloys with special reference to the lattice spacing of magnesium at high temperatures Locality: synthetic Sample: at T = 30 C Note: experiment #1 Journal of the Institute of Metals, 1939, 65, 477-485 |
| 9013057 | CIF | Mg | P 63/m m c | 3.2036; 3.2036; 5.2017 90; 90; 120 | 46.233 | Raynor, G. V.; Hume-Rothery W A technique for the X-ray powder photography of reactive metals and alloys with special reference to the lattice spacing of magnesium at high temperatures Locality: synthetic Sample: at T = 31.4 C Note: experiment #7 Journal of the Institute of Metals, 1939, 65, 477-485 |
| 9013058 | CIF | Mg | P 63/m m c | 3.2147; 3.2147; 5.2203 90; 90; 120 | 46.72 | Raynor, G. V.; Hume-Rothery W A technique for the X-ray powder photography of reactive metals and alloys with special reference to the lattice spacing of magnesium at high temperatures Locality: synthetic Sample: at T = 160 C Note: experiment #2 Journal of the Institute of Metals, 1939, 65, 477-485 |
| 9013059 | CIF | Mg | P 63/m m c | 3.2278; 3.2278; 5.2423 90; 90; 120 | 47.301 | Raynor, G. V.; Hume-Rothery W A technique for the X-ray powder photography of reactive metals and alloys with special reference to the lattice spacing of magnesium at high temperatures Locality: synthetic Sample: at T = 310.5 C Note: experiment #3 Journal of the Institute of Metals, 1939, 65, 477-485 |
| 9013060 | CIF | Mg | P 63/m m c | 3.242; 3.242; 5.2663 90; 90; 120 | 47.936 | Raynor, G. V.; Hume-Rothery W A technique for the X-ray powder photography of reactive metals and alloys with special reference to the lattice spacing of magnesium at high temperatures Locality: synthetic Sample: at T = 455 C Note: experiment #5 Journal of the Institute of Metals, 1939, 65, 477-485 |
| 9013061 | CIF | Mg | P 63/m m c | 3.2485; 3.2485; 5.2772 90; 90; 120 | 48.228 | Raynor, G. V.; Hume-Rothery W A technique for the X-ray powder photography of reactive metals and alloys with special reference to the lattice spacing of magnesium at high temperatures Locality: synthetic Sample: at T = 506.8 C Note: experiment #8 Journal of the Institute of Metals, 1939, 65, 477-485 |
| 9013062 | CIF | Mg | P 63/m m c | 3.2599; 3.2599; 5.296 90; 90; 120 | 48.74 | Raynor, G. V.; Hume-Rothery W A technique for the X-ray powder photography of reactive metals and alloys with special reference to the lattice spacing of magnesium at high temperatures Locality: synthetic Sample: at T = 597 C Note: experiment #9 Journal of the Institute of Metals, 1939, 65, 477-485 |
| 9013063 | CIF | Au0.8 Hg0.2 | F m -3 m | 4.126; 4.126; 4.126 90; 90; 90 | 70.241 | Owen, E. A.; O'Donnell Roberts E A The solubility of certain metals in gold Journal of the Institute of Metals, 1945, 71, 213-254 |
Back to the search form
Your own data is not in the COD? Deposit it, thanks!