Crystallography Open Database
Search results
Result: there are 795 entries in the selection
Switch to the old layout of the pageDownload all results as: list of COD numbers | list of CIF URLs | data in CSV format | archive of CIF files (ZIP)
Searching space group like 'I m -3 m'
COD ID  |
Links | Formula  |
Space group |
Cell parameters | Cell volume |
Bibliography |
|---|---|---|---|---|---|---|
| 9012876 | CIF | Rb | I m -3 m | 5.7; 5.7; 5.7 90; 90; 90 | 185.193 | Kelly, F. M.; Pearson, W. B. The rubidium transition at ~180 K Sample: at T = 297 K Note: specimen III lattice parameter for this T is estimated Canadian Journal of Physics, 1955, 33, 17-24 |
| 9012877 | CIF | Rb | I m -3 m | 5.609; 5.609; 5.609 90; 90; 90 | 176.464 | Kelly, F. M.; Pearson, W. B. The rubidium transition at ~180 K Sample: at T = 77 K Note: specimen IV Canadian Journal of Physics, 1955, 33, 17-24 |
| 9012878 | CIF | Rb | I m -3 m | 5.616; 5.616; 5.616 90; 90; 90 | 177.126 | Kelly, F. M.; Pearson, W. B. The rubidium transition at ~180 K Sample: at T = 90 K Note: specimen IV Canadian Journal of Physics, 1955, 33, 17-24 |
| 9012879 | CIF | Rb | I m -3 m | 5.697; 5.697; 5.697 90; 90; 90 | 184.901 | Kelly, F. M.; Pearson, W. B. The rubidium transition at ~180 K Sample: at T = 297 K Note: specimen IV lattice parameter for this T is estimated Canadian Journal of Physics, 1955, 33, 17-24 |
| 9012880 | CIF | Rb | I m -3 m | 5.607; 5.607; 5.607 90; 90; 90 | 176.275 | Kelly, F. M.; Pearson, W. B. The rubidium transition at ~180 K Sample: at T = 77 K Note: specimen VI Canadian Journal of Physics, 1955, 33, 17-24 |
| 9012916 | CIF | Ca | I m -3 m | 3.559; 3.559; 3.559 90; 90; 90 | 45.08 | Olijnyk, H.; Holzapfel, W. B. Phase transitions in alkaline earth metals under pressure Sample: P = 26.5 GPa Physics Letters, 1984, 191-194 |
| 9012924 | CIF | Ti | I m -3 m | 3.282; 3.282; 3.282 90; 90; 90 | 35.352 | Levinger, B. W. Lattice parameters of beta titanium at room temperature Sample: at T = 298 K, known as the beta phase Journal of Metals, 1953, 5, 195-195 |
| 9013134 | CIF | Se | I m -3 m | 2.822; 2.822; 2.822 90; 90; 90 | 22.474 | Akahama, Y.; Kobayashi, M.; Kawamura, H. Structural study on pressure-induced phase transition from beta-Po type to bcc in selenium at 140 GPa Locality: synthetic Sample: at P = 140 GPa Note: structure known as bcc, phase Se VI Japanese Journal of Applied Physics, 1992, 31, 1621-1624 |
| 9013135 | CIF | Se | I m -3 m | 2.8159; 2.8159; 2.8159 90; 90; 90 | 22.328 | Akahama, Y.; Kobayashi, M.; Kawamura, H. Structural study on pressure-induced phase transition from beta-Po type to bcc in selenium at 140 GPa Locality: synthetic Sample: at P = 142.5 GPa Note: structure known as bcc, phase Se VI Japanese Journal of Applied Physics, 1992, 31, 1621-1624 |
| 9013136 | CIF | Se | I m -3 m | 2.8076; 2.8076; 2.8076 90; 90; 90 | 22.131 | Akahama, Y.; Kobayashi, M.; Kawamura, H. Structural study on pressure-induced phase transition from beta-Po type to bcc in selenium at 140 GPa Locality: synthetic Sample: at P = 146.5 GPa Note: structure known as bcc, phase Se VI Japanese Journal of Applied Physics, 1992, 31, 1621-1624 |
| 9013137 | CIF | Se | I m -3 m | 2.7941; 2.7941; 2.7941 90; 90; 90 | 21.814 | Akahama, Y.; Kobayashi, M.; Kawamura, H. Structural study on pressure-induced phase transition from beta-Po type to bcc in selenium at 140 GPa Locality: synthetic Sample: at P = 150 GPa Note: structure known as bcc, phase Se VI Japanese Journal of Applied Physics, 1992, 31, 1621-1624 |
| 9013414 | CIF | Fe | I m -3 m | 2.858; 2.858; 2.858 90; 90; 90 | 23.345 | Davey, W. P. Lattice constants of twelve common metals Locality: synthetic Note: lattice parameter is average of runs 1 & 2 Physical Review, 1925, 25, 753-761 |
| 9013415 | CIF | Fe | I m -3 m | 2.855; 2.855; 2.855 90; 90; 90 | 23.271 | Davey, W. P. Lattice constants of twelve common metals Locality: synthetic Note: lattice parameter is average of runs 3 & 4 Physical Review, 1925, 25, 753-761 |
| 9013463 | CIF | Fe | I m -3 m | 2.8604; 2.8604; 2.8604 90; 90; 90 | 23.403 | Jette, E. R.; Foote, F. Precision determination of lattice constants Sample: at T = 25C Note: lattice parameter is average of four samples Journal of Chemical Physics, 1935, 3, 605-616 |
| 9013472 | CIF | Fe | I m -3 m | 2.869; 2.869; 2.869 90; 90; 90 | 23.615 | Basinski, Z. S.; Hume-Rothery W; Sutton, A. L. The lattice expansion of iron Sample: at T = 513 K Proceedings of the Royal Society of London A, 1955, 229, 459-467 |
| 9013473 | CIF | Fe | I m -3 m | 2.873; 2.873; 2.873 90; 90; 90 | 23.714 | Basinski, Z. S.; Hume-Rothery W; Sutton, A. L. The lattice expansion of iron Sample: at T = 623 K Proceedings of the Royal Society of London A, 1955, 229, 459-467 |
| 9013474 | CIF | Fe | I m -3 m | 2.878; 2.878; 2.878 90; 90; 90 | 23.838 | Basinski, Z. S.; Hume-Rothery W; Sutton, A. L. The lattice expansion of iron Sample: at T = 722 K Proceedings of the Royal Society of London A, 1955, 229, 459-467 |
| 9013475 | CIF | Fe | I m -3 m | 2.882; 2.882; 2.882 90; 90; 90 | 23.938 | Basinski, Z. S.; Hume-Rothery W; Sutton, A. L. The lattice expansion of iron Sample: at T = 822 K Proceedings of the Royal Society of London A, 1955, 229, 459-467 |
| 9013476 | CIF | Fe | I m -3 m | 2.886; 2.886; 2.886 90; 90; 90 | 24.037 | Basinski, Z. S.; Hume-Rothery W; Sutton, A. L. The lattice expansion of iron Sample: at T = 921 K Proceedings of the Royal Society of London A, 1955, 229, 459-467 |
| 9013477 | CIF | Fe | I m -3 m | 2.89; 2.89; 2.89 90; 90; 90 | 24.138 | Basinski, Z. S.; Hume-Rothery W; Sutton, A. L. The lattice expansion of iron Sample: at T = 994 K Proceedings of the Royal Society of London A, 1955, 229, 459-467 |
Back to the search form
Your own data is not in the COD? Deposit it, thanks!