Crystallography Open Database

Result : There are 10 entries in the selection

You can download the COD numbers of the selection as a text file

You can download all files as a single ZIP archive

Searching journal of publication like 'Journal of Physics F: Metal Physics'

COD ID: 9012033
CIF file Formula: - Be -
Comments: Ming, L. C.; Manghnani, M. H. Isothermal compression and phase transition in beryllium to 28.3 GPa Sample: at P = .001 GPa Note: BeI phase Journal of Physics F: Metal Physics 14 (1984) 1-8
Space group: P 63/m m c
Cell volume: 16.207
Cell parameters: 2.28; 2.28; 3.6; 90; 90; 120;  

COD ID: 9012034
CIF file Formula: - Be -
Comments: Ming, L. C.; Manghnani, M. H. Isothermal compression and phase transition in beryllium to 28.3 GPa Sample: at P = 5 GPa Note: BeI phase Journal of Physics F: Metal Physics 14 (1984) 1-8
Space group: P 63/m m c
Cell volume: 15.408
Cell parameters: 2.2526; 2.2526; 3.5064; 90; 90; 120;  

COD ID: 9012035
CIF file Formula: - Be -
Comments: Ming, L. C.; Manghnani, M. H. Isothermal compression and phase transition in beryllium to 28.3 GPa Sample: at P = 8.6 GPa Note: BeI phase Journal of Physics F: Metal Physics 14 (1984) 1-8
Space group: P 63/m m c
Cell volume: 15.252
Cell parameters: 2.2504; 2.2504; 3.4776; 90; 90; 120;  

COD ID: 9012036
CIF file Formula: - Be -
Comments: Ming, L. C.; Manghnani, M. H. Isothermal compression and phase transition in beryllium to 28.3 GPa Sample: at P = 11.5 GPa Note: BeI phase Journal of Physics F: Metal Physics 14 (1984) 1-8
Space group: P 63/m m c
Cell volume: 14.729
Cell parameters: 2.2207; 2.2207; 3.4488; 90; 90; 120;  

COD ID: 9012037
CIF file Formula: - Be -
Comments: Ming, L. C.; Manghnani, M. H. Isothermal compression and phase transition in beryllium to 28.3 GPa Sample: at P = 14.5 GPa Note: BeII phase, slightly distorded HCP Journal of Physics F: Metal Physics 14 (1984) 1-8
Space group: P 63/m m c
Cell volume: 58.984
Cell parameters: 4.4278; 4.4278; 3.474; 90; 90; 120;  

COD ID: 9012038
CIF file Formula: - Be -
Comments: Ming, L. C.; Manghnani, M. H. Isothermal compression and phase transition in beryllium to 28.3 GPa Sample: at P = 19.5 GPa Note: BeII phase, slightly distorded HCP Journal of Physics F: Metal Physics 14 (1984) 1-8
Space group: P 63/m m c
Cell volume: 57.049
Cell parameters: 4.4004; 4.4004; 3.402; 90; 90; 120;  

COD ID: 9012039
CIF file Formula: - Be -
Comments: Ming, L. C.; Manghnani, M. H. Isothermal compression and phase transition in beryllium to 28.3 GPa Sample: at P = 22 GPa Note: BeII phase, slightly distorded HCP Journal of Physics F: Metal Physics 14 (1984) 1-8
Space group: P 63/m m c
Cell volume: 56.339
Cell parameters: 4.3799; 4.3799; 3.3912; 90; 90; 120;  

COD ID: 9012040
CIF file Formula: - Be -
Comments: Ming, L. C.; Manghnani, M. H. Isothermal compression and phase transition in beryllium to 28.3 GPa Sample: at P = 25.5 GPa Note: BeII phase, slightly distorded HCP Journal of Physics F: Metal Physics 14 (1984) 1-8
Space group: P 63/m m c
Cell volume: 55.932
Cell parameters: 4.3571; 4.3571; 3.402; 90; 90; 120;  

COD ID: 9012041
CIF file Formula: - Be -
Comments: Ming, L. C.; Manghnani, M. H. Isothermal compression and phase transition in beryllium to 28.3 GPa Sample: at P = 28.3 GPa Note: BeII phase, slightly distorded HCP Journal of Physics F: Metal Physics 14 (1984) 1-8
Space group: P 63/m m c
Cell volume: 56.334
Cell parameters: 4.389; 4.389; 3.3768; 90; 90; 120;  

COD ID: 9013111
CIF file Formula: - Be -
Comments: Vijayakumar, V.; Godwal, B. K.; Vohra, Y. K.; Sikka, S. K.; Chidambaram, R. On the high-pressure phase transition in beryllium metal Sample: at P = 28.3 GPa Note: phase II Journal of Physics F: Metal Physics 14 (1984) L65-L68
Space group: P 21 21 2
Cell volume: 27.809
Cell parameters: 2.168; 3.755; 3.416; 90; 90; 90;  


Back to the search form
Your own data is not in the COD? Deposit it, thanks!
Top of the page