Crystallography Open Database

Result: there are 100 entries in the selection

Switch to the old layout of the page

Download all results as: list of COD numbers | list of CIF URLs | data in CSV format | archive of CIF files (ZIP)

Searching journal of publication like 'American Mineralogist' volume of publication is 77

Left arrow Left arrow First | Left arrow Previous 20 | of 5 | Next 20 Blue right arrow | Last Blue right arrow Blue right arrow | Display 5 20 50 100 200 300 500 1000 entries per page

COD ID Up arrow Links Formula Up arrow Space group Blue up arrow Cell parameters Cell volume Up arrow Bibliography
9001401 CIFB Na O8 Si3C -17.8388; 12.373; 6.8082
93.324; 116.381; 92.014		589.191Fleet, M. E.
Tetrahedral-site occupancies in reedmergnerite and synthetic boron albite (NaBSi3O8) sample from Utah
American Mineralogist, 1992, 77, 76-84
9001402 CIFB Na O8 Si2.9C -17.852; 12.35; 6.806
93.37; 116.3; 91.58		589.59Fleet, M. E.
Tetrahedral-site occupancies in reedmergnerite and synthetic boron albite (NaBSi3O8) sample low boron albite Gb100
American Mineralogist, 1992, 77, 76-84
9001403 CIFB Na O8 Si3C -17.91; 12.336; 6.82
93.54; 116.13; 90.6		595.799Fleet, M. E.
Tetrahedral-site occupancies in reedmergnerite and synthetic boron albite (NaBSi3O8) sample high boron albite Gb87
American Mineralogist, 1992, 77, 76-84
9001503 CIFCa0.04 Fe2 H2 Li0.83 Mg2.17 Na2.962 O24 Si8C 1 2/m 19.822; 17.836; 5.286
90; 104.37; 90		897.056Hawthorne, F. C.; Oberti, R.; Ungaretti, L.; Grice, J. D.
Leakeite, NaNa2(Mg2Fe2Li)Si8O22(OH)2, a new alkali amphibole from the Kajlidongri manganese mine, Jhabua district, Madhya Pradesh, India
American Mineralogist, 1992, 77, 1112-1115
9001504 CIFAl4 Ca H5 Mn O20 P3 SiC 1 2/m 117.188; 11.477; 7.322
90; 113.83; 90		1321.25Grice, J. D.; Dunn, P. J.
Attakolite: New data and crystal-structure determination
American Mineralogist, 1992, 77, 1285-1291
9001432 CIFAl2 Ni O4F d -3 m :28.05154; 8.05154; 8.05154
90; 90; 90		521.96Roelofsen, J. N.; Peterson, R. C.; Raudsepp, M.
Structural variation in nickel aluminate spinel (NiAl2O4) sample quench temperature = 1500 C, initially annealed at 800 C
American Mineralogist, 1992, 77, 522-528
9001433 CIFAl1.999 Ni0.999 O4F d -3 m :28.05221; 8.05221; 8.05221
90; 90; 90		522.09Roelofsen, J. N.; Peterson, R. C.; Raudsepp, M.
Structural variation in nickel aluminate spinel (NiAl2O4) sample quench temperature = 1400 C, initially annealed at 800 C
American Mineralogist, 1992, 77, 522-528
9001434 CIFAl2 Ni O4F d -3 m :28.05146; 8.05146; 8.05146
90; 90; 90		521.944Roelofsen, J. N.; Peterson, R. C.; Raudsepp, M.
Structural variation in nickel aluminate spinel (NiAl2O4) sample quench temperature = 1200 C, initially annealed at 800 C
American Mineralogist, 1992, 77, 522-528
9001435 CIFAl2.001 Ni0.999 O4F d -3 m :28.05038; 8.05038; 8.05038
90; 90; 90		521.734Roelofsen, J. N.; Peterson, R. C.; Raudsepp, M.
Structural variation in nickel aluminate spinel (NiAl2O4) sample quench temperature = 1100 C, initially annealed at 800 C
American Mineralogist, 1992, 77, 522-528
9001436 CIFAl2 Ni O4F d -3 m :28.04899; 8.04899; 8.04899
90; 90; 90		521.464Roelofsen, J. N.; Peterson, R. C.; Raudsepp, M.
Structural variation in nickel aluminate spinel (NiAl2O4) sample quench temperature = 1000 C, initially annealed at 800 C
American Mineralogist, 1992, 77, 522-528
9001437 CIFAl2.001 Ni1.001 O4F d -3 m :28.04741; 8.04741; 8.04741
90; 90; 90		521.157Roelofsen, J. N.; Peterson, R. C.; Raudsepp, M.
Structural variation in nickel aluminate spinel (NiAl2O4) sample quench temperature = 900 C, initially annealed at 800 C
American Mineralogist, 1992, 77, 522-528
9001438 CIFAl2 Ni O4F d -3 m :28.04622; 8.04622; 8.04622
90; 90; 90		520.926Roelofsen, J. N.; Peterson, R. C.; Raudsepp, M.
Structural variation in nickel aluminate spinel (NiAl2O4) sample quench temperature = 800 C, initially annealed at 800 C
American Mineralogist, 1992, 77, 522-528
9001439 CIFAl2.001 Ni0.999 O4F d -3 m :28.05263; 8.05263; 8.05263
90; 90; 90		522.172Roelofsen, J. N.; Peterson, R. C.; Raudsepp, M.
Structural variation in nickel aluminate spinel (NiAl2O4) sample quench temperature = 1500 C, initially annealed at 1300 C
American Mineralogist, 1992, 77, 522-528
9001440 CIFAl2 Ni O4F d -3 m :28.05199; 8.05199; 8.05199
90; 90; 90		522.047Roelofsen, J. N.; Peterson, R. C.; Raudsepp, M.
Structural variation in nickel aluminate spinel (NiAl2O4) sample quench temperature = 1300 C, initially annealed at 1300 C
American Mineralogist, 1992, 77, 522-528
9001441 CIFAl1.999 Ni1.001 O4F d -3 m :28.05145; 8.05145; 8.05145
90; 90; 90		521.942Roelofsen, J. N.; Peterson, R. C.; Raudsepp, M.
Structural variation in nickel aluminate spinel (NiAl2O4) sample quench temperature = 1200 C, initially annealed at 1300 C
American Mineralogist, 1992, 77, 522-528
9001442 CIFAl2 Ni O4F d -3 m :28.05059; 8.05059; 8.05059
90; 90; 90		521.775Roelofsen, J. N.; Peterson, R. C.; Raudsepp, M.
Structural variation in nickel aluminate spinel (NiAl2O4) sample quench temperature = 1100 C, initially annealed at 1300 C
American Mineralogist, 1992, 77, 522-528
9001443 CIFAl2.001 Ni1.001 O4F d -3 m :28.04897; 8.04897; 8.04897
90; 90; 90		521.46Roelofsen, J. N.; Peterson, R. C.; Raudsepp, M.
Structural variation in nickel aluminate spinel (NiAl2O4) sample quench temperature = 1000 C, initially annealed at 1300 C
American Mineralogist, 1992, 77, 522-528
9001444 CIFAl1.999 Ni1.001 O4F d -3 m :28.04751; 8.04751; 8.04751
90; 90; 90		521.176Roelofsen, J. N.; Peterson, R. C.; Raudsepp, M.
Structural variation in nickel aluminate spinel (NiAl2O4) sample quench temperature = 900 C, initially annealed at 1300 C
American Mineralogist, 1992, 77, 522-528
9001446 CIFFe2 Mg O4F d -3 m :28.3805; 8.3805; 8.3805
90; 90; 90		588.586O'Neill H St C; Annersten, H.; Virgo, D.
The temperature dependence of the cation distribution in magnesioferrite (MgFe2O4) from powder XRD structural refinements and Mossbauer spectroscopy batch 1, anneal T = 400 C using Rietveld method
American Mineralogist, 1992, 77, 725-740
9001447 CIFFe2 Mg O4F d -3 m :28.3806; 8.3806; 8.3806
90; 90; 90		588.607O'Neill H St C; Annersten, H.; Virgo, D.
The temperature dependence of the cation distribution in magnesioferrite (MgFe2O4) from powder XRD structural refinements and Mossbauer spectroscopy batch 2, anneal T = 450 C using Rietveld method
American Mineralogist, 1992, 77, 725-740

Left arrow Left arrow First | Left arrow Previous 20 | of 5 | Next 20 Blue right arrow | Last Blue right arrow Blue right arrow | Display 5 20 50 100 200 300 500 1000 entries per page

Back to the search form
Your own data is not in the COD? Deposit it, thanks!
Top of the page
All data in the COD and the database itself are dedicated to the public domain and licensed under the CC0 License . Users of the data should acknowledge the original authors of the structural data.