Result: there are 53 entries in the selection
Switch to the old layout of the pageDownload all results as: list of COD numbers | list of CIF URLs | data in CSV format | archive of CIF files (ZIP)
Searching journal of publication like 'Philosophical Magazine'
COD ID  |
Links | Formula  |
Space group |
Cell parameters | Cell volume |
Bibliography |
|---|---|---|---|---|---|---|
| 9012953 | CIF | Au | F m -3 m | 4.0699; 4.0699; 4.0699 90; 90; 90 | 67.414 | Owen, E. A.; Yates, E. L. Precision measurements of crystal parameters Sample: at T = 18 C Note: lattice parameter is mean value of 5 radiation types Philosophical Magazine, 1933, 15, 472-488 |
| 9012954 | CIF | Cu | F m -3 m | 3.6077; 3.6077; 3.6077 90; 90; 90 | 46.956 | Owen, E. A.; Yates, E. L. Precision measurements of crystal parameters Sample: at T = 18 C Note: lattice parameter is mean value of 2 radiation types Philosophical Magazine, 1933, 15, 472-488 |
| 9012955 | CIF | Al | F m -3 m | 4.0406; 4.0406; 4.0406 90; 90; 90 | 65.969 | Owen, E. A.; Yates, E. L. Precision measurements of crystal parameters Locality: synthetic Sample: at T = 18 C Note: lattice parameter is mean value of 4 radiation types Philosophical Magazine, 1933, 15, 472-488 |
| 9012957 | CIF | Pt | F m -3 m | 3.9158; 3.9158; 3.9158 90; 90; 90 | 60.043 | Owen, E. A.; Yates, E. L. Precision measurements of crystal parameters Sample: at T = 18 C Note: lattice parameter is mean value of 5 radiation types Philosophical Magazine, 1933, 15, 472-488 |
| 9012958 | CIF | Rh | F m -3 m | 3.7957; 3.7957; 3.7957 90; 90; 90 | 54.686 | Owen, E. A.; Yates, E. L. Precision measurements of crystal parameters Sample: at T = 18 C Note: lattice parameter is mean value of 3 radiation types Philosophical Magazine, 1933, 15, 472-488 |
| 9012959 | CIF | Pb | F m -3 m | 4.9396; 4.9396; 4.9396 90; 90; 90 | 120.525 | Owen, E. A.; Yates, E. L. Precision measurements of crystal parameters Sample: at T = 18 C Note: lattice parameter is mean value of 4 radiation types Philosophical Magazine, 1933, 15, 472-488 |
| 9012960 | CIF | Ir | F m -3 m | 3.8312; 3.8312; 3.8312 90; 90; 90 | 56.235 | Owen, E. A.; Yates, E. L. Precision measurements of crystal parameters Sample: at T = 18 C Note: lattice parameter is mean value of 3 radiation types Philosophical Magazine, 1933, 15, 472-488 |
| 9012961 | CIF | Ag | F m -3 m | 4.0772; 4.0772; 4.0772 90; 90; 90 | 67.778 | Owen, E. A.; Yates, E. L. Precision measurements of crystal parameters Sample: at T = 18 C Note: lattice parameter is mean value of 5 radiation types Philosophical Magazine, 1933, 15, 472-488 |
| 9012962 | CIF | Pd | F m -3 m | 3.8824; 3.8824; 3.8824 90; 90; 90 | 58.52 | Owen, E. A.; Yates, E. L. Precision measurements of crystal parameters Sample: at T = 18 C Note: lattice parameter is mean value of 4 radiation types Philosophical Magazine, 1933, 15, 472-488 |
| 9012963 | CIF | Ni | F m -3 m | 3.517; 3.517; 3.517 90; 90; 90 | 43.503 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 12 C Note: film 601 & 617 Philosophical Magazine, 1936, 21, 809-819 |
| 9012964 | CIF | Ni | F m -3 m | 3.517; 3.517; 3.517 90; 90; 90 | 43.503 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 13 C Note: film 563 & 608 Philosophical Magazine, 1936, 21, 809-819 |
| 9012965 | CIF | Ni | F m -3 m | 3.517; 3.517; 3.517 90; 90; 90 | 43.503 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 14 C Note: films 569, 574, 596, 597 Philosophical Magazine, 1936, 21, 809-819 |
| 9012966 | CIF | Ni | F m -3 m | 3.517; 3.517; 3.517 90; 90; 90 | 43.503 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 15 C Note: films 560, 562, 621, 625, 626 Philosophical Magazine, 1936, 21, 809-819 |
| 9012967 | CIF | Ni | F m -3 m | 3.5171; 3.5171; 3.5171 90; 90; 90 | 43.507 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 16 C Note: film 590 Philosophical Magazine, 1936, 21, 809-819 |
| 9012968 | CIF | Ni | F m -3 m | 3.5172; 3.5172; 3.5172 90; 90; 90 | 43.51 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 18 C Philosophical Magazine, 1936, 21, 809-819 |
| 9012969 | CIF | Ni | F m -3 m | 3.5212; 3.5212; 3.5212 90; 90; 90 | 43.659 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 98 C Note: film 565 Philosophical Magazine, 1936, 21, 809-819 |
| 9012970 | CIF | Ni | F m -3 m | 3.5259; 3.5259; 3.5259 90; 90; 90 | 43.834 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 187 C Note: film 567 Philosophical Magazine, 1936, 21, 809-819 |
| 9012971 | CIF | Ni | F m -3 m | 3.5295; 3.5295; 3.5295 90; 90; 90 | 43.968 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 257 C Note: film 573 Philosophical Magazine, 1936, 21, 809-819 |
| 9012972 | CIF | Ni | F m -3 m | 3.5302; 3.5302; 3.5302 90; 90; 90 | 43.994 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 275 C Note: film 595 Philosophical Magazine, 1936, 21, 809-819 |
| 9012973 | CIF | Ni | F m -3 m | 3.5319; 3.5319; 3.5319 90; 90; 90 | 44.058 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 301 C Note: film 564 Philosophical Magazine, 1936, 21, 809-819 |
| 9012974 | CIF | Ni | F m -3 m | 3.5335; 3.5335; 3.5335 90; 90; 90 | 44.118 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 331 C Note: film 594 Philosophical Magazine, 1936, 21, 809-819 |
| 9012975 | CIF | Ni | F m -3 m | 3.5337; 3.5337; 3.5337 90; 90; 90 | 44.125 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 333 C Note: film 571 Philosophical Magazine, 1936, 21, 809-819 |
| 9012976 | CIF | Ni | F m -3 m | 3.5337; 3.5337; 3.5337 90; 90; 90 | 44.125 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 336 C Note: film 584 Philosophical Magazine, 1936, 21, 809-819 |
| 9012977 | CIF | Ni | F m -3 m | 3.5338; 3.5338; 3.5338 90; 90; 90 | 44.129 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 338 C Note: film 606 Philosophical Magazine, 1936, 21, 809-819 |
| 9012978 | CIF | Ni | F m -3 m | 3.5343; 3.5343; 3.5343 90; 90; 90 | 44.148 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 341 C Note: film 611 Philosophical Magazine, 1936, 21, 809-819 |
| 9012979 | CIF | Ni | F m -3 m | 3.5343; 3.5343; 3.5343 90; 90; 90 | 44.148 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 342 C Note: film 585 Philosophical Magazine, 1936, 21, 809-819 |
| 9012980 | CIF | Ni | F m -3 m | 3.5342; 3.5342; 3.5342 90; 90; 90 | 44.144 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 343 C Note: film 618 Philosophical Magazine, 1936, 21, 809-819 |
| 9012981 | CIF | Ni | F m -3 m | 3.5345; 3.5345; 3.5345 90; 90; 90 | 44.155 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 345 C Note: film 616 & 610 Philosophical Magazine, 1936, 21, 809-819 |
| 9012982 | CIF | Ni | F m -3 m | 3.5347; 3.5347; 3.5347 90; 90; 90 | 44.163 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 346 C Note: film 614 Philosophical Magazine, 1936, 21, 809-819 |
| 9012983 | CIF | Ni | F m -3 m | 3.5346; 3.5346; 3.5346 90; 90; 90 | 44.159 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 348 C Note: film 605 Philosophical Magazine, 1936, 21, 809-819 |
| 9012984 | CIF | Ni | F m -3 m | 3.5347; 3.5347; 3.5347 90; 90; 90 | 44.163 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 349 C Note: film 586 Philosophical Magazine, 1936, 21, 809-819 |
| 9012985 | CIF | Ni | F m -3 m | 3.535; 3.535; 3.535 90; 90; 90 | 44.174 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 352 C Note: film 612 Philosophical Magazine, 1936, 21, 809-819 |
| 9012986 | CIF | Ni | F m -3 m | 3.5355; 3.5355; 3.5355 90; 90; 90 | 44.193 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 356 C Note: film 624 Philosophical Magazine, 1936, 21, 809-819 |
| 9012987 | CIF | Ni | F m -3 m | 3.5356; 3.5356; 3.5356 90; 90; 90 | 44.197 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 359 C Note: film 592 Philosophical Magazine, 1936, 21, 809-819 |
| 9012988 | CIF | Ni | F m -3 m | 3.5359; 3.5359; 3.5359 90; 90; 90 | 44.208 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 362 C Note: film 599 Philosophical Magazine, 1936, 21, 809-819 |
| 9012989 | CIF | Ni | F m -3 m | 3.536; 3.536; 3.536 90; 90; 90 | 44.212 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 363 C Note: film 600 Philosophical Magazine, 1936, 21, 809-819 |
| 9012990 | CIF | Ni | F m -3 m | 3.5361; 3.5361; 3.5361 90; 90; 90 | 44.215 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 365 C Note: film 593 Philosophical Magazine, 1936, 21, 809-819 |
| 9012991 | CIF | Ni | F m -3 m | 3.5367; 3.5367; 3.5367 90; 90; 90 | 44.238 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 370 C Note: film 577 & 598 Philosophical Magazine, 1936, 21, 809-819 |
| 9012992 | CIF | Ni | F m -3 m | 3.5367; 3.5367; 3.5367 90; 90; 90 | 44.238 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 373 C Note: film 576 Philosophical Magazine, 1936, 21, 809-819 |
| 9012993 | CIF | Ni | F m -3 m | 3.5367; 3.5367; 3.5367 90; 90; 90 | 44.238 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 374 C Note: film 603 Philosophical Magazine, 1936, 21, 809-819 |
| 9012994 | CIF | Ni | F m -3 m | 3.5371; 3.5371; 3.5371 90; 90; 90 | 44.253 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 378 C Note: film 604 Philosophical Magazine, 1936, 21, 809-819 |
| 9012995 | CIF | Ni | F m -3 m | 3.5379; 3.5379; 3.5379 90; 90; 90 | 44.283 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 388 C Note: film 589 Philosophical Magazine, 1936, 21, 809-819 |
| 9012996 | CIF | Ni | F m -3 m | 3.5383; 3.5383; 3.5383 90; 90; 90 | 44.298 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 398 C Note: film 556 Philosophical Magazine, 1936, 21, 809-819 |
| 9012997 | CIF | Ni | F m -3 m | 3.5386; 3.5386; 3.5386 90; 90; 90 | 44.309 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 405 C Note: film 613 Philosophical Magazine, 1936, 21, 809-819 |
| 9012998 | CIF | Ni | F m -3 m | 3.5388; 3.5388; 3.5388 90; 90; 90 | 44.317 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 410 C Note: film 607 Philosophical Magazine, 1936, 21, 809-819 |
| 9012999 | CIF | Ni | F m -3 m | 3.5388; 3.5388; 3.5388 90; 90; 90 | 44.317 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample at T = 411 C Note: film 609 Philosophical Magazine, 1936, 21, 809-819 |
| 9013000 | CIF | Ni | F m -3 m | 3.5402; 3.5402; 3.5402 90; 90; 90 | 44.369 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 429 C Note: film 591 Philosophical Magazine, 1936, 21, 809-819 |
| 9013001 | CIF | Ni | F m -3 m | 3.5422; 3.5422; 3.5422 90; 90; 90 | 44.445 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 460 C Note: film 572 Philosophical Magazine, 1936, 21, 809-819 |
| 9013002 | CIF | Ni | F m -3 m | 3.5448; 3.5448; 3.5448 90; 90; 90 | 44.543 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 501 C Note: film 561 Philosophical Magazine, 1936, 21, 809-819 |
| 9013003 | CIF | Ni | F m -3 m | 3.5481; 3.5481; 3.5481 90; 90; 90 | 44.667 | Owen, E. A.; Yates, E. L. X-ray measurement of the thermal expansion of pure nickel Sample: at T = 557 C Note: film 575 Philosophical Magazine, 1936, 21, 809-819 |