COD ID | Links | Formula | Space group | Cell parameters | Cell volume | Bibliography |
---|---|---|---|---|---|---|
9017431 | CIF | Fe Se2 | P n n m | 4.698; 5.667; 3.5088 90; 90; 90 | 93.417 | Lavina, B.; Downs, R. T.; Sinogeikin, S. The structure of ferroselite, FeSe2, at pressures up to 46 GPa and temperatures down to 50 K: A single-crystal micro-diffraction analysis Note: P = 8.1 GPa Crystals, 2018, 8 |
9017432 | CIF | Fe Se2 | P n n m | 4.603; 5.581; 3.4492 90; 90; 90 | 88.608 | Lavina, B.; Downs, R. T.; Sinogeikin, S. The structure of ferroselite, FeSe2, at pressures up to 46 GPa and temperatures down to 50 K: A single-crystal micro-diffraction analysis Note: P = 17.3 GPa Crystals, 2018, 8 |
9017433 | CIF | Fe Se2 | P n n m | 4.555; 5.524; 3.409 90; 90; 90 | 85.777 | Lavina, B.; Downs, R. T.; Sinogeikin, S. The structure of ferroselite, FeSe2, at pressures up to 46 GPa and temperatures down to 50 K: A single-crystal micro-diffraction analysis Note: P = 24.4 GPa Crystals, 2018, 8 |
9017434 | CIF | Fe Se2 | P n n m | 4.488; 5.471; 3.3734 90; 90; 90 | 82.83 | Lavina, B.; Downs, R. T.; Sinogeikin, S. The structure of ferroselite, FeSe2, at pressures up to 46 GPa and temperatures down to 50 K: A single-crystal micro-diffraction analysis Note: P = 32 GPa Crystals, 2018, 8 |
9017435 | CIF | Fe Se2 | P n n m | 4.404; 5.391; 3.3185 90; 90; 90 | 78.788 | Lavina, B.; Downs, R. T.; Sinogeikin, S. The structure of ferroselite, FeSe2, at pressures up to 46 GPa and temperatures down to 50 K: A single-crystal micro-diffraction analysis Note: P = 46 GPa Crystals, 2018, 8 |
9017436 | CIF | Fe Se2 | P n n m | 4.7885; 5.7782; 3.5821 90; 90; 90 | 99.113 | Lavina, B.; Downs, R. T.; Sinogeikin, S. The structure of ferroselite, FeSe2, at pressures up to 46 GPa and temperatures down to 50 K: A single-crystal micro-diffraction analysis Note: T = 198.2 K, P = 0.0001 GPa Crystals, 2018, 8 |
9017437 | CIF | Fe Se2 | P n n m | 4.7893; 5.7775; 3.5795 90; 90; 90 | 99.045 | Lavina, B.; Downs, R. T.; Sinogeikin, S. The structure of ferroselite, FeSe2, at pressures up to 46 GPa and temperatures down to 50 K: A single-crystal micro-diffraction analysis Note: T = 148.4 K, P = 0.0001 GPa Crystals, 2018, 8 |
9017438 | CIF | Fe Se2 | P n n m | 4.7834; 5.7767; 3.5789 90; 90; 90 | 98.893 | Lavina, B.; Downs, R. T.; Sinogeikin, S. The structure of ferroselite, FeSe2, at pressures up to 46 GPa and temperatures down to 50 K: A single-crystal micro-diffraction analysis Note: T = 50.4 K, P = 0.0001 GPa Crystals, 2018, 8 |
9017439 | CIF | Fe Se2 | P n n m | 4.751; 5.723; 3.5501 90; 90; 90 | 96.527 | Lavina, B.; Downs, R. T.; Sinogeikin, S. The structure of ferroselite, FeSe2, at pressures up to 46 GPa and temperatures down to 50 K: A single-crystal micro-diffraction analysis Note: T = 197 K, P = 3.68 GPa Crystals, 2018, 8 |
9017440 | CIF | Fe Se2 | P n n m | 4.7446; 5.772; 3.5512 90; 90; 90 | 97.253 | Lavina, B.; Downs, R. T.; Sinogeikin, S. The structure of ferroselite, FeSe2, at pressures up to 46 GPa and temperatures down to 50 K: A single-crystal micro-diffraction analysis Note: T = 116 K, P = 3.64 GPa Crystals, 2018, 8 |
9017441 | CIF | Fe H Li O5 P | P -1 | 5.3528; 7.2896; 5.1187 109.359; 97.733; 106.359 | 174.984 | Marx, N.; Croguennec, L.; Carlier, D.; Wattiaux, A.; Le Cras, F.; Suard, E.; Delmas, C. The structure of tavorite LiFePO4(OH) from diffraction and GGA + U studies and its preliminary electrochemical characterization Dalton Transactions, 2010, 39, 5108-5116 |
9017442 | CIF | Al K O8 Si3 | C 1 2/m 1 | 8.578; 12.978; 7.204 90; 116.02; 90 | 720.699 | Gering, E. Silizium/Aluminium-Ordnung und Kristallperfektion von Sanidinen Note: Sample ORMA, X-Ray diffraction Dissertation Kernforshungszentrum Karlsruhe, 1985, 1, 1-97 |
9017443 | CIF | Al K O8 Si3 | C 1 2/m 1 | 8.543; 13.019; 7.183 90; 115.99; 90 | 718.11 | Gering, E. Silizium/Aluminium-Ordnung und Kristallperfektion von Sanidinen Note: Sample SVG1, neutron diffraction Dissertation Kernforshungszentrum Karlsruhe, 1985, 1, 1-97 |
9017444 | CIF | Al K O8 Si3 | C 1 2/m 1 | 8.543; 13.019; 7.183 90; 115.99; 90 | 718.11 | Gering, E. Silizium/Aluminium-Ordnung und Kristallperfektion von Sanidinen Note: Sample SAGA, X-ray diffraction Dissertation Kernforshungszentrum Karlsruhe, 1985, 1, 1-97 |
9017445 | CIF | Al K O8 Si3 | C 1 2/m 1 | 8.543; 13.019; 7.183 90; 115.99; 90 | 718.11 | Gering, E. Silizium/Aluminium-Ordnung und Kristallperfektion von Sanidinen Note: Sample SANU, neutron diffraction Dissertation Kernforshungszentrum Karlsruhe, 1985, 1, 1-97 |
9017446 | CIF | Al K O8 Si3 | C 1 2/m 1 | 8.543; 13.019; 7.183 90; 115.99; 90 | 718.11 | Gering, E. Silizium/Aluminium-Ordnung und Kristallperfektion von Sanidinen Note: Sample STOT, T = 650 C, X-ray diffraction Dissertation Kernforshungszentrum Karlsruhe, 1985, 1, 1-97 |
9017447 | CIF | Al K O8 Si3 | C 1 2/m 1 | 8.544; 13.026; 7.18 90; 115.97; 90 | 718.402 | Gering, E. Silizium/Aluminium-Ordnung und Kristallperfektion von Sanidinen Note: Sample SATO, T = 750 C, X-ray diffraction Dissertation Kernforshungszentrum Karlsruhe, 1985, 1, 1-97 |
9017448 | CIF | Al K O8 Si3 | C 1 2/m 1 | 8.545; 13.026; 7.179 90; 115.97; 90 | 718.386 | Gering, E. Silizium/Aluminium-Ordnung und Kristallperfektion von Sanidinen Note: Sample SANG, T = 850 C, nuetron diffraction Dissertation Kernforshungszentrum Karlsruhe, 1985, 1, 1-97 |
9017449 | CIF | Al K O8 Si3 | C 1 2/m 1 | 8.545; 13.026; 7.179 90; 115.97; 90 | 718.386 | Gering, E. Silizium/Aluminium-Ordnung und Kristallperfektion von Sanidinen Note: Sample SAND, T = 850 C, X-ray diffraction Dissertation Kernforshungszentrum Karlsruhe, 1985, 1, 1-97 |
9017450 | CIF | Al K O8 Si3 | C 1 2/m 1 | 8.545; 13.026; 7.179 90; 115.97; 90 | 718.386 | Gering, E. Silizium/Aluminium-Ordnung und Kristallperfektion von Sanidinen Note: Sample SAAT, T = 1050 C, X-ray diffraction Dissertation Kernforshungszentrum Karlsruhe, 1985, 1, 1-97 |