Crystallography Open Database

Result: there are 57 entries in the selection

Switch to the old layout of the page

Download all results as: list of COD numbers | list of CIF URLs | data in CSV format | archive of CIF files (ZIP)

Searching journal of publication like 'Physical Review'

Left arrow Left arrow First | Left arrow Previous 20 | of 3 | Next 20 Blue right arrow | Last Blue right arrow Blue right arrow | Display 5 20 50 100 200 300 500 1000 entries per page

COD ID Up arrow Links Formula Up arrow Space group Up arrow Cell parameters Cell volume Blue up arrow Bibliography
9011615 CIFCoP 63/m m c2.519; 2.519; 4.091
90; 90; 120		22.481Marick, L.
Variation of resistance and structure of cobalt with temperature and a discussion of its photoelectric emission Sample: at room T Note: cell edge a is average of photographs 1 & 2
Physical Review, 1936, 49, 831-837
9011616 CIFCoP 63/m m c2.527; 2.527; 4.119
90; 90; 120		22.779Marick, L.
Variation of resistance and structure of cobalt with temperature and a discussion of its photoelectric emission Sample: at T = 295 C Note: photograph 3
Physical Review, 1936, 49, 831-837
9011617 CIFCoP 63/m m c2.536; 2.536; 4.136
90; 90; 120		23.036Marick, L.
Variation of resistance and structure of cobalt with temperature and a discussion of its photoelectric emission Sample: at T = 420 C Note: photograph 4
Physical Review, 1936, 49, 831-837
9013415 CIFFeI m -3 m2.855; 2.855; 2.855
90; 90; 90		23.271Davey, W. P.
Lattice constants of twelve common metals Locality: synthetic Note: lattice parameter is average of runs 3 & 4
Physical Review, 1925, 25, 753-761
9013414 CIFFeI m -3 m2.858; 2.858; 2.858
90; 90; 90		23.345Davey, W. P.
Lattice constants of twelve common metals Locality: synthetic Note: lattice parameter is average of runs 1 & 2
Physical Review, 1925, 25, 753-761
9011598 CIFCrI m -3 m2.91; 2.91; 2.91
90; 90; 90		24.642Hull, A. W.; Davey, W. P.
Crystal structure of chromium
Physical Review, 1919, 14, 540-540
9011601 CIFVI m -3 m3.04; 3.04; 3.04
90; 90; 90		28.094Hull, A. W.
Crystal structures of vanadium, germanium and graphite
Physical Review, 1922, 20, 113-113
9011599 CIFZnP 63/m m c2.67; 2.67; 4.966
90; 90; 120		30.659Hull, A. W.; Davey, W. P.
Graphical determination of hexagonal and tetragonal crystal structures from X-ray data
Physical Review, 1921, 17, 549-570
9011606 CIFMoI m -3 m3.136; 3.136; 3.136
90; 90; 90		30.841Davey, W. P.
Lattice constants of twelve common metals Locality: synthetic Note: lattice parameter is average of runs 3 & 4
Physical Review, 1925, 25, 753-761
9011605 CIFMoI m -3 m3.142; 3.142; 3.142
90; 90; 90		31.018Davey, W. P.
Lattice constants of twelve common metals Locality: synthetic Note: lattice parameter is average of runs 1 & 2
Physical Review, 1925, 25, 753-761
9011609 CIFWI m -3 m3.155; 3.155; 3.155
90; 90; 90		31.405Davey, W. P.
Lattice constants of twelve common metals Locality: synthetic Note: lattice parameter is average of runs 1 & 2
Physical Review, 1925, 25, 753-761
9011610 CIFWI m -3 m3.157; 3.157; 3.157
90; 90; 90		31.465Davey, W. P.
Lattice constants of twelve common metals Locality: synthetic Note: run 3
Physical Review, 1925, 25, 753-761
9011611 CIFWI m -3 m3.158; 3.158; 3.158
90; 90; 90		31.495Davey, W. P.
Lattice constants of twelve common metals Locality: synthetic Note: lattice parameter is average of runs 3 & 4
Physical Review, 1925, 25, 753-761
9011600 CIFTiP 63/m m c2.97; 2.97; 4.72
90; 90; 120		36.057Hull, A. W.
Crystal structure of titanium, zirconium, cerium, thorium and osmium
Physical Review, 1921, 18, 88-89
9017801 CIFLiI m -3 m3.47851; 3.47851; 3.47851
90; 90; 90		42.09Berliner, R.; Fajen, O.; Smith, H. G.; Hitterman, R. L.
Neutron powder-diffraction studies of lithium, sodium and potassium metal Note: Body-centered cubic, T = 20 K
Physical Review, 1989, 12086-12097
9011603 CIFNiF m -3 m3.499; 3.499; 3.499
90; 90; 90		42.838Davey, W. P.
Lattice constants of twelve common metals Locality: synthetic Note: lattice parameter is average of runs 1 & 2
Physical Review, 1925, 25, 753-761
9011628 CIFLiI m -3 m3.5; 3.5; 3.5
90; 90; 90		42.875Barrett, C. S.
A low temperature transformation in lithium Sample: at T = -196 C
Physical Review, 1947, 72, 245-245
9011597 CIFNiF m -3 m3.52; 3.52; 3.52
90; 90; 90		43.614Hull, A. W.
A new method of x-ray crystal analysis
Physical Review, 1917, 10, 661-696
9011618 CIFCoF m -3 m3.559; 3.559; 3.559
90; 90; 90		45.08Marick, L.
Variation of resistance and structure of cobalt with temperature and a discussion of its photoelectric emission Sample: at room T Note: cell parameter is average of photographs 5-8
Physical Review, 1936, 49, 831-837
9011619 CIFCoF m -3 m3.573; 3.573; 3.573
90; 90; 90		45.614Marick, L.
Variation of resistance and structure of cobalt with temperature and a discussion of its photoelectric emission Sample: at T = 295 C Note: photograph 9
Physical Review, 1936, 49, 831-837

Left arrow Left arrow First | Left arrow Previous 20 | of 3 | Next 20 Blue right arrow | Last Blue right arrow Blue right arrow | Display 5 20 50 100 200 300 500 1000 entries per page

Back to the search form
Your own data is not in the COD? Deposit it, thanks!