Crystallography Open Database
Search results
Result: there are 57 entries in the selection
Switch to the old layout of the pageDownload all results as: list of COD numbers | list of CIF URLs | data in CSV format | archive of CIF files (ZIP)
Searching journal of publication like 'Physical Review'
COD ID  |
Links | Formula  |
Space group |
Cell parameters | Cell volume |
Bibliography |
|---|---|---|---|---|---|---|
| 1508402 | CIF | H3 Li O6 Se2 | P 1 n 1 | 6.25; 7.88; 5.43 90; 105.2; 90 | 258 | Vedam, K.; Okaya, Y.; Pepinsky, R. Crystal structure of ferroelectric LiH3(SeO3)2 Physical Review, 1960, 119, 1252-1255 |
| 9009237 | CIF | H2 K O4 P | F d d 2 | 10.53; 10.44; 6.9 90; 90; 90 | 758.539 | Levy, H. A.; Peterson, S. W.; Simonsen, S. H. Neutron diffraction study of the ferroelectric modification of potassium dihydrogen phosphate Note sample at T = 113 K Physical Review, 1954, 93, 1120-1121 |
| 9011597 | CIF | Ni | F m -3 m | 3.52; 3.52; 3.52 90; 90; 90 | 43.614 | Hull, A. W. A new method of x-ray crystal analysis Physical Review, 1917, 10, 661-696 |
| 9011598 | CIF | Cr | I m -3 m | 2.91; 2.91; 2.91 90; 90; 90 | 24.642 | Hull, A. W.; Davey, W. P. Crystal structure of chromium Physical Review, 1919, 14, 540-540 |
| 9011599 | CIF | Zn | P 63/m m c | 2.67; 2.67; 4.966 90; 90; 120 | 30.659 | Hull, A. W.; Davey, W. P. Graphical determination of hexagonal and tetragonal crystal structures from X-ray data Physical Review, 1921, 17, 549-570 |
| 9011600 | CIF | Ti | P 63/m m c | 2.97; 2.97; 4.72 90; 90; 120 | 36.057 | Hull, A. W. Crystal structure of titanium, zirconium, cerium, thorium and osmium Physical Review, 1921, 18, 88-89 |
| 9011601 | CIF | V | I m -3 m | 3.04; 3.04; 3.04 90; 90; 90 | 28.094 | Hull, A. W. Crystal structures of vanadium, germanium and graphite Physical Review, 1922, 20, 113-113 |
| 9011602 | CIF | Al | F m -3 m | 4.046; 4.046; 4.046 90; 90; 90 | 66.233 | Davey, W. P. Lattice constants of twelve common metals Locality: synthetic Note: lattice parameter is average of runs 1 & 2 Physical Review, 1925, 25, 753-761 |
| 9011603 | CIF | Ni | F m -3 m | 3.499; 3.499; 3.499 90; 90; 90 | 42.838 | Davey, W. P. Lattice constants of twelve common metals Locality: synthetic Note: lattice parameter is average of runs 1 & 2 Physical Review, 1925, 25, 753-761 |
| 9011604 | CIF | Cu | F m -3 m | 3.597; 3.597; 3.597 90; 90; 90 | 46.539 | Davey, W. P. Lattice constants of twelve common metals Locality: synthetic Note: lattice parameter is average of runs 1,2 & 3 Physical Review, 1925, 25, 753-761 |
| 9011605 | CIF | Mo | I m -3 m | 3.142; 3.142; 3.142 90; 90; 90 | 31.018 | Davey, W. P. Lattice constants of twelve common metals Locality: synthetic Note: lattice parameter is average of runs 1 & 2 Physical Review, 1925, 25, 753-761 |
| 9011606 | CIF | Mo | I m -3 m | 3.136; 3.136; 3.136 90; 90; 90 | 30.841 | Davey, W. P. Lattice constants of twelve common metals Locality: synthetic Note: lattice parameter is average of runs 3 & 4 Physical Review, 1925, 25, 753-761 |
| 9011607 | CIF | Ag | F m -3 m | 4.079; 4.079; 4.079 90; 90; 90 | 67.867 | Davey, W. P. Lattice constants of twelve common metals Locality: synthetic Note: lattice parameter is average of runs 1 & 2 Physical Review, 1925, 25, 753-761 |
| 9011608 | CIF | Ag | F m -3 m | 4.058; 4.058; 4.058 90; 90; 90 | 66.825 | Davey, W. P. Lattice constants of twelve common metals Locality: synthetic Note: lattice parameter is average of runs 3 & 4 Physical Review, 1925, 25, 753-761 |
| 9011609 | CIF | W | I m -3 m | 3.155; 3.155; 3.155 90; 90; 90 | 31.405 | Davey, W. P. Lattice constants of twelve common metals Locality: synthetic Note: lattice parameter is average of runs 1 & 2 Physical Review, 1925, 25, 753-761 |
| 9011610 | CIF | W | I m -3 m | 3.157; 3.157; 3.157 90; 90; 90 | 31.465 | Davey, W. P. Lattice constants of twelve common metals Locality: synthetic Note: run 3 Physical Review, 1925, 25, 753-761 |
| 9011611 | CIF | W | I m -3 m | 3.158; 3.158; 3.158 90; 90; 90 | 31.495 | Davey, W. P. Lattice constants of twelve common metals Locality: synthetic Note: lattice parameter is average of runs 3 & 4 Physical Review, 1925, 25, 753-761 |
| 9011612 | CIF | Au | F m -3 m | 4.065; 4.065; 4.065 90; 90; 90 | 67.171 | Davey, W. P. Lattice constants of twelve common metals Locality: synthetic Note: lattice parameter is average of runs 1 & 2 Physical Review, 1925, 25, 753-761 |
| 9011613 | CIF | Au | F m -3 m | 4.073; 4.073; 4.073 90; 90; 90 | 67.568 | Davey, W. P. Lattice constants of twelve common metals Locality: synthetic Note: lattice parameter is average of runs 1,2 & 3 Physical Review, 1925, 25, 753-761 |
| 9011614 | CIF | Bi | P 63/m m c | 4.539; 4.539; 11.829 90; 90; 120 | 211.057 | Davey, W. P. Lattice constants of twelve common metals Locality: synthetic Note: lattice parameter is average of runs 1 & 2 Physical Review, 1925, 25, 753-761 |
| 9011615 | CIF | Co | P 63/m m c | 2.519; 2.519; 4.091 90; 90; 120 | 22.481 | Marick, L. Variation of resistance and structure of cobalt with temperature and a discussion of its photoelectric emission Sample: at room T Note: cell edge a is average of photographs 1 & 2 Physical Review, 1936, 49, 831-837 |
| 9011616 | CIF | Co | P 63/m m c | 2.527; 2.527; 4.119 90; 90; 120 | 22.779 | Marick, L. Variation of resistance and structure of cobalt with temperature and a discussion of its photoelectric emission Sample: at T = 295 C Note: photograph 3 Physical Review, 1936, 49, 831-837 |
| 9011617 | CIF | Co | P 63/m m c | 2.536; 2.536; 4.136 90; 90; 120 | 23.036 | Marick, L. Variation of resistance and structure of cobalt with temperature and a discussion of its photoelectric emission Sample: at T = 420 C Note: photograph 4 Physical Review, 1936, 49, 831-837 |
| 9011618 | CIF | Co | F m -3 m | 3.559; 3.559; 3.559 90; 90; 90 | 45.08 | Marick, L. Variation of resistance and structure of cobalt with temperature and a discussion of its photoelectric emission Sample: at room T Note: cell parameter is average of photographs 5-8 Physical Review, 1936, 49, 831-837 |
| 9011619 | CIF | Co | F m -3 m | 3.573; 3.573; 3.573 90; 90; 90 | 45.614 | Marick, L. Variation of resistance and structure of cobalt with temperature and a discussion of its photoelectric emission Sample: at T = 295 C Note: photograph 9 Physical Review, 1936, 49, 831-837 |
| 9011620 | CIF | Co | F m -3 m | 3.579; 3.579; 3.579 90; 90; 90 | 45.844 | Marick, L. Variation of resistance and structure of cobalt with temperature and a discussion of its photoelectric emission Sample: at T = 420 C Note: photograph 10 Physical Review, 1936, 49, 831-837 |
| 9011621 | CIF | Co | F m -3 m | 3.589; 3.589; 3.589 90; 90; 90 | 46.23 | Marick, L. Variation of resistance and structure of cobalt with temperature and a discussion of its photoelectric emission Sample: at T = 625 C Note: photograph 11 Physical Review, 1936, 49, 831-837 |
| 9011622 | CIF | Co | F m -3 m | 3.602; 3.602; 3.602 90; 90; 90 | 46.734 | Marick, L. Variation of resistance and structure of cobalt with temperature and a discussion of its photoelectric emission Sample: at T = 843 C Note: photograph 12 Physical Review, 1936, 49, 831-837 |
| 9011623 | CIF | Co | F m -3 m | 3.617; 3.617; 3.617 90; 90; 90 | 47.32 | Marick, L. Variation of resistance and structure of cobalt with temperature and a discussion of its photoelectric emission Sample: at T = 1099 C Note: photograph 13 Physical Review, 1936, 49, 831-837 |
| 9011624 | CIF | Co | F m -3 m | 3.628; 3.628; 3.628 90; 90; 90 | 47.753 | Marick, L. Variation of resistance and structure of cobalt with temperature and a discussion of its photoelectric emission Sample: at T = 1121 C Note: photograph 14 Physical Review, 1936, 49, 831-837 |
| 9011625 | CIF | Co | F m -3 m | 3.644; 3.644; 3.644 90; 90; 90 | 48.388 | Marick, L. Variation of resistance and structure of cobalt with temperature and a discussion of its photoelectric emission Sample: at T = 1148 C Note: photograph 15 Physical Review, 1936, 49, 831-837 |
| 9011626 | CIF | Co | F m -3 m | 3.647; 3.647; 3.647 90; 90; 90 | 48.507 | Marick, L. Variation of resistance and structure of cobalt with temperature and a discussion of its photoelectric emission Sample: at T = 1187 C Note: photograph 16 Physical Review, 1936, 49, 831-837 |
| 9011627 | CIF | Li | F m -3 m | 4.41; 4.41; 4.41 90; 90; 90 | 85.766 | Barrett, C. S. A low temperature transformation in lithium Sample: at T = -196 C Note: transformation induced by metal being plastically deformed Physical Review, 1947, 72, 245-245 |
| 9011628 | CIF | Li | I m -3 m | 3.5; 3.5; 3.5 90; 90; 90 | 42.875 | Barrett, C. S. A low temperature transformation in lithium Sample: at T = -196 C Physical Review, 1947, 72, 245-245 |
| 9011629 | CIF | Ge | F d -3 m :1 | 5.65745; 5.65745; 5.65745 90; 90; 90 | 181.077 | Smakula, A.; Kalnajs, J. Precision determination of lattice constants with a Geiger-counter X-ray diffractometer Sample: at T = 25 C Physical Review, 1955, 99, 1737-1743 |
| 9011630 | CIF | He | P 63/m m c | 3.53; 3.53; 5.76 90; 90; 120 | 62.159 | Henshaw, D. G. Structure of solid helium by neutron diffraction Sample: at T = 1.1 K and P = .007 GPa Physical Review, 1958, 109, 328-330 |
| 9011631 | CIF | He | I m -3 m | 4.01; 4.01; 4.01 90; 90; 90 | 64.481 | Schuch, A. F.; Grilly, E. R.; Mills, R. L. Structure of the alpha and beta forms of solid He Sample: at T = 1.9 K & P = .01 GPa Note: structure known as the alpha form Physical Review, 1958, 110, 775-775 |
| 9011632 | CIF | He | P 63/m m c | 3.46; 3.46; 5.6 90; 90; 120 | 58.059 | Schuch, A. F.; Grilly, E. R.; Mills, R. L. Structure of the alpha and beta forms of solid He Sample: at T = 3.3 K & P = .018 GPa Note: structure known as the beta form Physical Review, 1958, 110, 775-775 |
| 9011633 | CIF | Ne | F m -3 m | 4.462; 4.462; 4.462 90; 90; 90 | 88.836 | Bolz, L. H.; Mauer, F. A. Measurement of the lattice constants of neon isotopes in the temperature range 4-24 K Locality: synthetic Sample: at T = 4.2 K Note: this is isotope 20 Ne Physical Review, 1962, 111, 242-249 |
| 9011634 | CIF | Ne | F m -3 m | 4.454; 4.454; 4.454 90; 90; 90 | 88.359 | Bolz, L. H.; Mauer, F. A. Measurement of the lattice constants of neon isotopes in the temperature range 4-24 K Locality: synthetic Sample: at T = 4.2 K Note: this is isotope 22 Ne Physical Review, 1962, 111, 242-249 |
| 9011635 | CIF | Ar | F m -3 m | 5.25; 5.25; 5.25 90; 90; 90 | 144.703 | Henshaw, D. G. Atomic distribution in liquid and solid neon and solid argon by neutron diffraction Locality: synthetic Sample: at T = 4.2 K Physical Review, 1958, 111, 1470-1475 |
| 9013414 | CIF | Fe | I m -3 m | 2.858; 2.858; 2.858 90; 90; 90 | 23.345 | Davey, W. P. Lattice constants of twelve common metals Locality: synthetic Note: lattice parameter is average of runs 1 & 2 Physical Review, 1925, 25, 753-761 |
| 9013415 | CIF | Fe | I m -3 m | 2.855; 2.855; 2.855 90; 90; 90 | 23.271 | Davey, W. P. Lattice constants of twelve common metals Locality: synthetic Note: lattice parameter is average of runs 3 & 4 Physical Review, 1925, 25, 753-761 |
| 9013416 | CIF | Pd | F m -3 m | 3.859; 3.859; 3.859 90; 90; 90 | 57.468 | Davey, W. P. Lattice constants of twelve common metals Locality: synthetic Note: lattice parameter is average of runs 1 & 2 Physical Review, 1925, 25, 753-761 |
| 9013417 | CIF | Pt | F m -3 m | 3.912; 3.912; 3.912 90; 90; 90 | 59.868 | Davey, W. P. Lattice constants of twelve common metals Locality: synthetic Note: lattice parameter is average of three runs Physical Review, 1925, 25, 753-761 |
| 9013418 | CIF | Pb | F m -3 m | 4.92; 4.92; 4.92 90; 90; 90 | 119.095 | Davey, W. P. Lattice constants of twelve common metals Locality: synthetic Note: lattice parameter is average of runs 1 & 2 Physical Review, 1925, 25, 753-761 |
| 9014273 | CIF | Ba O3 Ti | P 4 m m | 3.986; 3.986; 4.026 90; 90; 90 | 63.966 | Shirane, G.; Danner, H.; Pepinsky, R. Neutron diffraction study of orthorhombic BaTiO3 Note: tetragonal structure Physical Review, 1957, 105, 856-860 |
| 9014284 | CIF | Br2 Fe | P -3 m 1 | 3.772; 3.772; 6.223 90; 90; 120 | 76.679 | Wilkinson, M. K.; Cable, J. W.; Wollan, E. O.; Koehler, W. C. Neutron diffraction investigations of the magnetic ordering in FeBr2, CoBr2, FeCl2, and CoCl2 Physical Review, 1959, 113, 497-507 |
| 9014719 | CIF | Cl2 Co | R -3 m :H | 3.553; 3.553; 17.359 90; 90; 120 | 189.778 | Wilkinson, M. K.; Cable, J. W.; Wollan, E. O.; Koehler, W. C. Neutron diffraction investigations of the magnetic ordering in FeBr2, CoBr2, FeCl2, and CoCl2 Physical Review, 1959, 113, 497-507 |
| 9014774 | CIF | Ba O3 Ti | A m m 2 | 3.99; 5.669; 5.682 90; 90; 90 | 128.523 | Shirane, G.; Danner, H.; Pepinsky, R. Neutron diffraction study of orthorhombic BaTiO3 Note: orthorhombic structure Physical Review, 1957, 105, 856-860 |
Back to the search form
Your own data is not in the COD? Deposit it, thanks!